Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Transparent/translucent PC for light diffusion special effects. Thicker sections without sinks. Internal mold release. Pigment package may affect properties. Application testing always recommended
This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
物性信息：
| 密度 | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.35 % @Temperature 23.0 °C | 0.35 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 熔体流动速率 | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C | 6.0 g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 抗张强度(断裂) | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 |
| 抗张强度(屈服) | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 伸长率 (断裂) | 120 % | 120 % | 50 mm/min; ISO 527 |
| 屈服伸长率 | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 拉伸模量 | 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 |
| 弯曲强度 | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 弯曲模量 | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 悬壁梁缺口冲击强度 | 12.0 kJ/m² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A |
| 70.0 kJ/m² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| 简支梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/2C | |
| 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 体积电阻率 | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| 介电强度 | 17.0 kV/mm @Thickness 3.20 mm | 432 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 |
| 线形热膨胀系数 - 流动 | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 74.6 µm/m-°C @Temperature 23.0 - 80.0 °C | 41.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Hot Ball Pressure Test | <= 140 °C | <= 284 °F | IEC 60695-10-2 |
| 载荷下热变形温度(0.46 MPa) | 138 °C | 280 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 载荷下热变形温度(1.8 MPa) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 维卡软化温度 | 144 °C | 291 °F | Rate B/50; ISO 306 |
| 145 °C | 293 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | HB @Thickness 0.700 mm | HB @Thickness 0.0276 in | UL 94 |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | 2nd value; UL 94 | |
| 极限氧指数 | 25 % | 25 % | LOI; ISO 4589 |
| 灼热丝试验 | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | Glow Wire Flammability Index; IEC 60695-2-12 |
| 折射率 | 1.586 | 1.586 | ISO 489 |
| 雾度 | <= 0.80 % @Thickness 2.54 mm | <= 0.80 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 88 - 90 % @Thickness 2.54 mm | 88 - 90 % @Thickness 0.100 in | ASTM D 1003 |
| 球压试验，125°C+/-2℃ | PASSES | IEC 60695-10-2 |
熔融酯交换缩聚法
在熔融酯交换缩聚法制备聚碳酸酯的工艺中，参与反应的两种单体分别为双酚A和碳酸二苯酯。其反应过程可分为酯交换阶段和缩聚阶段。
两阶段分别要求温度180~200℃，压力270~400Pa，反应1~3h以达到80~90%的转化率以及290~300℃，130Pa以下条件以加深反应程度。反应过程均为可逆平衡反应。
为获得预期分子量的聚碳酸酯，起始碳酸二本酯须过量，且须不间断并尽可能多地从反应物系中移出反应生成的低分子产物苯酚来调节两基团数量比，控制分子量。
主营塑胶原料：PC , PPA , POM , PA6 , PA66 , PBT , PET , PC/ABS , PMMA ,TPSIV , GPPS , HIPS , PP , PE , EVA , EAA , PPO , PA11, PA12 , TPU , TPV , TPEE, POE , PPS , LCP
一般项目：合成材料销售；合成纤维销售；工程塑料及合成树脂销售；塑料制品销售；生物基材料销售；高性能纤维及复合材料销售；玻璃纤维增强塑料制品销售。（除依法须经批准的项目外，凭营业执照依法自主开展经营活动）
本公司长期经营各种塑胶原料. 长期经营的品牌有杜邦,旭化成,GE,三菱,巴斯夫,LG,东丽,LNP,南亚,帝人,拜耳,台湾长春，台湾奇美，台湾台化等 通用塑料：ABS、AS、GPPS、HIPS、PP、PE、食品级ABS、AS、PS、PP等。工程塑料：COC镜头料、PMMA、POM、PC、PC/ABS、PA66、PA6、PPE、PBT、PET、ASA、PPO、PC PBT、PBT/PC 、CA；PA46、PA9T、PA6T、PA12、PA...