熔指 8.5 紫外稳定剂SABIC Innovative Plastics Lexan® 193 PC沙伯基础

SABIC Innovative Plastics Lexan® 193 PC

Polycarbonate (PC)

SABIC Innovative Plastics (GE Plastics)

产品说明：

Nonhalogenated. 8.5 MFR. High impact. Thick wall sections. UV-stabilized. Opaques only.

This data was supplied by SABIC-IP for the Americas region.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法比重1.19 g/cc1.19 g/ccASTM D 792吸水率0.19 %

@Time 86400 sec

0.19 %

@Time 24.0 hour

ASTM D 570Moisture Absorption at E %

@Temperature 23.0 °C

0.37 %

@Temperature 73.4 °F

ASTM D 570
0.54 %

@Temperature 100 °C

0.54 %

@Temperature 212 °F

ASTM D 570线性成型收缩率,Flow0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm

0.0050 - 0.0070 in/in

@Thickness 0.126 in

SABIC Method熔体流动速率8.5 g/10 min

@Load 1.20 kg, Temperature 300 °C

8.5 g/10 min

@Load 2.65 lb, Temperature 572 °F

ASTM D 1238机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）6868ASTM D 785洛氏硬度（R 级）118118ASTM D 785抗张强度(断裂)63.0 MPa9140 psiType I, 50 mm/min; ASTM D 638抗张强度(屈服)58.0 MPa8410 psiType I, 50 mm/min; ASTM D 638伸长率 (断裂)115 %115 %Type I, 50 mm/min; ASTM D 638屈服伸长率7.0 %7.0 %Type I, 50 mm/min; ASTM D 638弯曲强度81.0 MPa11700 psi1.3 mm/min, 50 mm span; ASTM D 790弯曲模量2.13 GPa309 ksi1.3 mm/min, 50 mm span; ASTM D 790悬壁梁缺口冲击强度7.47 J/cm

@Temperature 23.0 °C

14.0 ft-lb/in

@Temperature 73.4 °F

ASTM D 256悬壁梁无缺口冲击强度32.04 J/cm

@Temperature 23.0 °C

60.02 ft-lb/in

@Temperature 73.4 °F

ASTM D 4812拉伸冲击强度420 kJ/m²200 ft-lb/in²Type S; ASTM D 1822落锤总能量169 J

@Temperature 23.0 °C

125 ft-lb

@Temperature 73.4 °F

ASTM D 3029泰伯磨损，毫克/1000次20

@Load 1.00 kg

20

@Load 2.20 lb

CS-17; ASTM D 1044电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率2.50e+17 ohm-cm2.50e+17 ohm-cmASTM D 257介电常数3.0

@Frequency 1.00e+6 Hz

3.0

@Frequency 1.00e+6 Hz

ASTM D 150介电强度16.3 kV/mm

@Thickness 3.20 mm

414 kV/in

@Thickness 0.126 in

in air; ASTM D 149耗散因数0.00090

@Frequency 50.0 - 60.0 Hz

0.00090

@Frequency 50.0 - 60.0 Hz

ASTM D 150
0.010

@Frequency 1.00e+6 Hz

0.010

@Frequency 1.00e+6 Hz

ASTM D 150热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动64.8 µm/m-°C

@Temperature -40.0 - 95.0 °C

36.0 µin/in-°F

@Temperature -40.0 - 203 °F

ASTM E 831载荷下热变形温度(0.46 MPa)137 °C

@Thickness 6.40 mm

279 °F

@Thickness 0.252 in

unannealed; ASTM D 648载荷下热变形温度(1.8 MPa)126 °C

@Thickness 6.40 mm

259 °F

@Thickness 0.252 in

unannealed; ASTM D 648