Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Polycarbonate with high flow, good processability, good impact and thermal properties, non-Chlorine and non-Bromine flame retardant, UL rated V-0 and V-1. Available in limited translucent colors only.
物性信息：
| 比重 | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| 水分吸收 | 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.24 % | 0.24 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 25 g/10 min @Load 1.20 kg, Temperature 300 °C | 25 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| 化合物熔体指数 | 24 g/10 min @Load 1.20 kg, Temperature 300 °C | 24 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| 抗张强度(断裂) | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
| 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 | |
| 抗张强度(屈服) | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
| 伸长率 (断裂) | 98 % | 98 % | 50 mm/min; ISO 527 |
| 102 % | 102 % | Type I, 50 mm/min; ASTM D638 | |
| 屈服伸长率 | 5.8 % | 5.8 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 | |
| 拉伸模量 | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| 2.25 GPa | 326 ksi | 50 mm/min; ASTM D638 | |
| 弯曲强度 | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 弯曲模量 | 2.20 GPa | 319 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 7.10 J/cm | 13.3 ft-lb/in | ASTM D256 |
| 2.30 J/cm @Temperature -30.0 °C | 4.31 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*3; ISO 180/1A | |
| 21.0 kJ/m² @Temperature -30.0 °C | 9.99 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | 184 kJ/m² | 87.6 ft-lb/in² | 80*10*3; ISO 180/1U |
| 183 kJ/m² @Temperature -30.0 °C | 87.1 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1U | |
| 落锤总能量 | 65.0 J @Temperature 23.0 °C | 47.9 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| 相比耐漏电起痕指数(CTI) | 175 - 250 V | 175 - 250 V | UL 746A |
| 线形热膨胀系数 - 流动 | 68.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 37.8 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 71.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 39.4 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 线性热膨胀系数,横向流动 | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 69.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.3 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| 载荷下热变形温度(1.8 MPa) | 120 °C @Thickness 3.20 mm | 248 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| 维卡软化温度 | 136 °C | 277 °F | Rate B/50; ASTM D1525 |
| 137 °C | 279 °F | Rate B/50; ISO 306 | |
| 138 °C | 280 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-1 @Thickness 1.00 mm | V-1 @Thickness 0.0394 in | UL 94 |
| V-0 @Thickness 1.20 mm | V-0 @Thickness 0.0472 in | UL 94 |
| 球压试验，125°C+/-2℃ | Pass | IEC 60695-10-2 |
东莞市晨希塑胶原料有限公司
主营塑胶原料：PC , PPA , POM , PA6 , PA66 , PBT , PET , PC/ABS , PMMA ,TPSIV , GPPS , HIPS , PP , PE , EVA , EAA , PPO , PA11, PA12 , TPU , TPV , TPEE, POE , PPS , LCP
一般项目：合成材料销售；合成纤维销售；工程塑料及合成树脂销售；塑料制品销售；生物基材料销售；高性能纤维及复合材料销售；玻璃纤维增强塑料制品销售。（除依法须经批准的项目外，凭营业执照依法自主开展经营活动）
本公司长期经营各种塑胶原料. 长期经营的品牌有杜邦,旭化成,GE,三菱,巴斯夫,LG,东丽,LNP,南亚,帝人,拜耳,台湾长春，台湾奇美，台湾台化等 通用塑料：ABS、AS、GPPS、HIPS、PP、PE、食品级ABS、AS、PS、PP等。工程塑料：COC镜头料、PMMA、POM、PC、PC/ABS、PA66、PA6、PPE、PBT、PET、ASA、PPO、PC PBT、PBT/PC 、CA；PA46、PA9T、PA6T、PA12、PA...