NORYLN225X 沙伯基础PPON225X
- 供应商
- 东莞市湘远塑胶有限公司
- 认证
- 品牌
- 沙伯基础
- 型号
- N225X
- 性能
- 尺寸稳定性良好 水解稳定
- 手机号
- 13532886152
- 销售经理
- 汪修建
- 所在地
- 深圳市龙岗区龙城街道盛平村委田段心南十二巷2号101
- 更新时间
- 2024-06-07 07:00
ppo 沙伯基础ppon225x
物性信息:
比重 | 1.11 g/cc | 1.11 g/cc | astm d792 |
线性成型收缩率,flow | 0.0050 - 0.0070 cm/cm @thickness 3.20 mm | 0.0050 - 0.0070 in/in @thickness 0.126 in | sabic method |
线性成型收缩率,横向 | 0.0050 - 0.0070 cm/cm @thickness 3.20 mm | 0.0050 - 0.0070 in/in @thickness 0.126 in | sabic method |
抗张强度(断裂) | 49.0 mpa | 7110 psi | type i, 50 mm/min; astm d638 |
抗张强度(屈服) | 66.0 mpa | 9570 psi | type i, 50 mm/min; astm d638 |
伸长率 (断裂) | 17 % | 17 % | type i, 50 mm/min; astm d638 |
屈服伸长率 | 8.0 % | 8.0 % | type i, 50 mm/min; astm d638 |
弯曲强度 | 99.0 mpa | 14400 psi | 2.6 mm/min, 100 mm span; astm d790 |
弯曲模量 | 2.49 gpa | 361 ksi | 2.6 mm/min, 100 mm span; astm d790 |
悬壁梁缺口冲击强度 | 1.86 j/cm | 3.48 ft-lb/in | astm d256 |
0.960 j/cm @temperature -30.0 °c | 1.80 ft-lb/in @temperature -22.0 °f | astm d256 | |
8.86 j/cm @thickness 3.20 mm | 16.6 ft-lb/in @thickness 0.126 in | astm d256 | |
落锤总能量 | 39.0 j | 28.8 ft-lb | instrumented impact energy @ peak; astm d3763 |
11.0 j @temperature -30.0 °c | 8.11 ft-lb @temperature -22.0 °f | instrumented impact energy @ peak; astm d3763 |
体积电阻率 | 2.80e+16 ohm-cm | 2.80e+16 ohm-cm | astm d257 |
表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | astm d257 |
介电常数 | 2.55 @frequency 1.00e+6 hz | 2.55 @frequency 1.00e+6 hz | astm d150 |
2.69 @frequency 50.0 - 60.0 hz | 2.69 @frequency 50.0 - 60.0 hz | astm d150 | |
介电强度 | 16.2 kv/mm @thickness 3.20 mm | 411 kv/in @thickness 0.126 in | in oil; astm d149 |
耗散因数 | 0.0070 @frequency 1.00e+6 hz | 0.0070 @frequency 1.00e+6 hz | astm d150 |
0.010 @frequency 50.0 - 60.0 hz | 0.010 @frequency 50.0 - 60.0 hz | astm d150 | |
耐电弧性 | 60 - 120 sec | 60 - 120 sec | tungsten; astm d495 |
相比耐漏电起痕指数(cti) | 400 - 600 v | 400 - 600 v | ul 746a |
热丝引燃 (hwi) | 60 - 120 sec | 60 - 120 sec | ul 746a |
高电弧燃烧,hai | >= 120 arcs | >= 120 arcs | ul 746a |
高压电弧跟踪率,hvtr |