polystyrene (ps)
sabic innovative plastics (ge plastics)
产品说明：
ppe+ps blend. unfilled. halogen-free fr performance. ul94v0/5va. ul746c f1. dielectric strength. suitable for e/e marketindoor/outdoor applications.
物性信息：
| 比重 | 1.11 g/cc | 1.11 g/cc | astm d792 |
| 线性成型收缩率,flow | 0.0050 - 0.0070 cm/cm @thickness 3.20 mm | 0.0050 - 0.0070 in/in @thickness 0.126 in | sabic method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @thickness 3.20 mm | 0.0050 - 0.0070 in/in @thickness 0.126 in | sabic method |
| 抗张强度(断裂) | 49.0 mpa | 7110 psi | type i, 50 mm/min; astm d638 |
| 抗张强度(屈服) | 66.0 mpa | 9570 psi | type i, 50 mm/min; astm d638 |
| 伸长率 (断裂) | 17 % | 17 % | type i, 50 mm/min; astm d638 |
| 屈服伸长率 | 8.0 % | 8.0 % | type i, 50 mm/min; astm d638 |
| 弯曲强度 | 99.0 mpa | 14400 psi | 2.6 mm/min, 100 mm span; astm d790 |
| 弯曲模量 | 2.49 gpa | 361 ksi | 2.6 mm/min, 100 mm span; astm d790 |
| 悬壁梁缺口冲击强度 | 1.86 j/cm | 3.48 ft-lb/in | astm d256 |
| 0.960 j/cm @temperature -30.0 °c | 1.80 ft-lb/in @temperature -22.0 °f | astm d256 | |
| 8.86 j/cm @thickness 3.20 mm | 16.6 ft-lb/in @thickness 0.126 in | astm d256 | |
| 落锤总能量 | 39.0 j | 28.8 ft-lb | instrumented impact energy @ peak; astm d3763 |
| 11.0 j @temperature -30.0 °c | 8.11 ft-lb @temperature -22.0 °f | instrumented impact energy @ peak; astm d3763 |
| 体积电阻率 | 2.80e+16 ohm-cm | 2.80e+16 ohm-cm | astm d257 |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | astm d257 |
| 介电常数 | 2.55 @frequency 1.00e+6 hz | 2.55 @frequency 1.00e+6 hz | astm d150 |
| 2.69 @frequency 50.0 - 60.0 hz | 2.69 @frequency 50.0 - 60.0 hz | astm d150 | |
| 介电强度 | 16.2 kv/mm @thickness 3.20 mm | 411 kv/in @thickness 0.126 in | in oil; astm d149 |
| 耗散因数 | 0.0070 @frequency 1.00e+6 hz | 0.0070 @frequency 1.00e+6 hz | astm d150 |
| 0.010 @frequency 50.0 - 60.0 hz | 0.010 @frequency 50.0 - 60.0 hz | astm d150 | |
| 耐电弧性 | 60 - 120 sec | 60 - 120 sec | tungsten; astm d495 |
| 相比耐漏电起痕指数(cti) | 400 - 600 v | 400 - 600 v | ul 746a |
| 热丝引燃 (hwi) | 60 - 120 sec | 60 - 120 sec | ul 746a |
| 高电弧燃烧，hai | >= 120 arcs | >= 120 arcs | ul 746a |
| 高压电弧跟踪率，hvtr | >= 150 mm/min | >= 5.91 in/min | ul 746a |
| 载荷下热变形温度(0.46 mpa) | 109 °c @thickness 6.40 mm | 228 °f @thickness 0.252 in | unannealed; astm d648 |
| 载荷下热变形温度(1.8 mpa) | 99.0 °c @thickness 6.40 mm | 210 °f @thickness 0.252 in | unannealed; astm d648 |
| 维卡软化温度 | 128 °c | 262 °f | rate b/50; astm d1525 |
| ul rti | 95.0 °c | 203 °f | ul 746b |
| ul rti，机械冲击 | 80.0 °c | 176 °f | ul 746b |
| ul rti，机械无冲击 | 95.0 °c | 203 °f | ul 746b |
| 可燃性(ul94) | hb @thickness 0.400 mm | hb @thickness 0.0157 in | ul 94 |
| v-0 @thickness 1.47 mm | v-0 @thickness 0.0579 in | ul 94 | |
| 5va @thickness 2.99 mm | 5va @thickness 0.118 in | ul 9 |