注塑级 peek 德国赢创德固赛 2000cf30 碳纤增强30% 耐化学聚醚醚酮

vestakeep®2000 cf30

polyetheretherketone

evonik industries ag

30% 碳纤维增强材料

产品说明：

carbon fiber-reinforced (30%) polyether ether ketone
vestakeep 2000 cf30 is a medium-viscosity, carbon fiber-reinforced(30%) polyether ether ketone for injection molding.
the semi-crystalline polymer features superior mechanical, thermal,and chemical resistance. parts made from vestakeep 2000 cf30 areself-extinguishing.
vestakeep 2000 cf30 can be processed by common injection moldingmachines for thermoplastics.
we recommend a melt temperature between 380°c and 400°c during theinjection molding process. the mold temperature should be within arange of 160°c to 200°c, preferably 180°c.

物性信息：

基本信息

填料/增强材料	碳纤维增强材料, 30% 填料按重量
特性	半结晶 耐化学性良好 中等粘性 自熄
形式	颗粒
加工方法	注射成型

物理性能额定值单位制测试方法

密度	1.38	g/cm³	iso 1183
溶化体积流率（mvr） (380°c/5.0 kg)	10.0	cm³/10min	iso 1133
收缩率 1			iso 294-4
垂直流动方向 : 180°c, 2.00mm	0.40	%	iso 294-4
流动方向 : 180°c, 2.00mm	0.0	%	iso 294-4

机械性能额定值单位制测试方法

拉伸模量	23000	mpa	iso 527-2
拉伸应力 (断裂)	240	mpa	iso 527-2
拉伸应变 (断裂)	2.0	%	iso 527-2

冲击性能额定值单位制测试方法

简支梁缺口冲击强度			iso 179/1ea
-30°c,完全断裂	8.0	kj/m²	iso 179/1ea
23°c,完全断裂	9.0	kj/m²	iso 179/1ea
简支梁无缺口冲击强度			iso 179/1eu
-30°c,完全断裂	45	kj/m²	iso 179/1eu
23°c,完全断裂	45	kj/m²	iso 179/1eu

热性能额定值单位制测试方法

热变形温度
0.45 mpa,未退火	340	°c	iso 75-2/b
1.8 mpa,未退火	330	°c	iso 75-2/a
维卡软化温度
--	343	°c	iso 306/a
--	340	°c	iso 306/b
熔融温度 2	340	°c	iso 11357-3
线形热膨胀系数 - 流动 (23 到 55°c)	1.0e-5	cm/cm/°c	iso 11359-2

电气性能额定值单位制测试方法

表面电阻率	1.0e+5	ohms	iec 60093
体积电阻率	1.0e+6	ohms·cm	iec 60093

可燃性额定值单位制测试方法

ul 阻燃等级 (1.60 mm)	v-0		ul 94
灼热丝易燃指数 (2.00 mm)	960	°c	iec 60695-2-12
热灯丝点火温度 (2.00 mm)	875	°c	iec 60695-2-13