耐化学 evonik 2000g 德国赢创德固赛 peek 中粘度 自熄 半结晶

vestakeep®2000g

polyetheretherketone

evonik industries ag

产品说明：

medium-viscosity, unreinforced polyether ether ketone
vestakeep 2000g is a medium-viscosity, unreinforced polyether etherketone for injection molding.
the semi-crystalline polymer features superior thermal and chemicalresistance. parts made from vestakeep 2000g areself-extinguishing.
vestakeep 2000g can be processed by common injection moldingmachines for thermoplastics.
we recommend a melt temperature between 360°c and 380°c during theinjection molding process. the mold temperature should be within arange of 160°c to 200°c, preferably 180°c.

物性信息：

基本信息

黄卡编号	e100203-100947904
特性	半结晶 耐化学性良好 中等粘性 自熄
形式	颗粒
加工方法	注射成型

物理性能额定值单位制测试方法

密度	1.30	g/cm³	iso 1183
溶化体积流率（mvr） (380°c/5.0 kg)	70.0	cm³/10min	iso 1133
收缩率 1			iso 294-4
垂直流动方向 : 80°c, 2.00mm	1.1	%	iso 294-4
流动方向 : 80°c, 2.00mm	1.1	%	iso 294-4

机械性能额定值单位制测试方法

拉伸模量	3700	mpa	iso 527-2
拉伸应力 (屈服)	100	mpa	iso 527-2
拉伸应变			iso 527-2
屈服	5.0	%	iso 527-2
断裂	30	%	iso 527-2

冲击性能额定值单位制测试方法

简支梁缺口冲击强度			iso 179/1ea
-30°c,完全断裂	6.0	kj/m²	iso 179/1ea
23°c,完全断裂	6.0	kj/m²	iso 179/1ea
简支梁无缺口冲击强度 (23°c)	无断裂		iso 179/1eu

热性能额定值单位制测试方法

维卡软化温度
--	335	°c	iso 306/a
--	310	°c	iso 306/b
熔融温度 2	340	°c	iso 11357-3
线形热膨胀系数 - 流动 (23 到 55°c)	6.0e-5	cm/cm/°c	iso 11359-2

电气性能额定值单位制测试方法

表面电阻率	1.0e+14	ohms	iec 60093
体积电阻率	1.0e+15	ohms·cm	iec 60093
介电强度 3	16	kv/mm	iec 60243-1
相对电容率			iec 60250
50 hz	2.80		iec 60250
1 mhz	2.80		iec 60250
漏电起痕指数			iec 60112
解决方案a 4	175	v	iec 60112
解决方案 a	200	v	iec 60112