产品说明：
lexan 945 polycarbonate (pc) resin is a non-filled, injectionmoldable grade. this non-chlorinated, non-brominated flameretardant pc has an ul-94 v0 rating and is available inue color options. lexan 945 is a general purpose resin designedto meet the needs of various applications.
物性信息：
基本信息
黄卡编号e121562-220906
e121562-100305095
添加剂阻燃性
特性chlorine free
通用
无溴
阻燃性
用途通用
外观不透明
可用颜色
加工方法注射成型
多点数据coefficient of thermal expansion vs. temperature (astm e831)
flexural dma (astm d4065)
pressure-volume-temperature (pvt - zoller method)
shear dma (astm d4065)
specific heat vs. temperature (astm d3417)
tensile fatigue
tensile stress vs. strain (astm d638)
thermal conductivity vs. temperature (astm e1530)
viscosity vs. shear rate (astm d3835)
物理性能额定值单位制测试方法比重1.19g/cm³astm d792熔流率（熔体流动速率） (300°c/1.2 kg)10g/10 minastm d1238收缩率 - 流动 (3.20 mm)0.60 到 0.80%内部方法
机械性能额定值单位制测试方法拉伸模量 12280mpaastm d638抗张强度 2
astm d638 屈服62.1mpaastm d638 断裂65.5mpaastm d638伸长率 3
astm d638 屈服6.0%astm d638 断裂130%astm d638弯曲模量 4(50.0mm 跨距)2340mpaastm d790弯曲强度 5(屈服,50.0 mm 跨距)101mpaastm d790
冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°c)800j/mastm d256装有测量仪表的落镖冲击 (23°c, totalenergy)73.4jastm d3763
热性能额定值单位制测试方法载荷下热变形温度
astm d648 0.45 mpa, 未退火, 3.20mm138°castm d648 1.8 mpa, 未退火, 3.20mm127°castm d648维卡软化温度143°castm d1525 6线形热膨胀系数
astm e831 流动 : -40 到40°c6.7e-5cm/cm/°castm e831 横向 : -40 到40°c6.7e-5cm/cm/°castm e831rti elec130°cul 746rti imp120°cul 746rti130°cul 746
电气性能额定值单位制测试方法耐电弧性 7plc 7
astm d495相比耐漏电起痕指数(cti)plc 2
ul 746高电弧燃烧指数(hai)plc 3
ul 746高电压电弧起痕速率 (hvtr)plc 4
ul 746热丝引燃 (hwi)plc 2
ul 746
可燃性额定值单位制测试方法ul 阻燃等级
ul 94 0.800 mmv-2
ul 94 1.14 mmv-0
ul 94 3.05 mm5va
ul 94灼热丝易燃指数 (1.00 mm)960°ciec 60695-2-12热灯丝点火温度 (1.00 mm)875°ciec 60695-2-13极限氧指数35%iso 4589-2
注射额定值单位制
干燥温度121°c
干燥时间3.0 到 4.0hr
干燥时间，*大48hr
建议的*大水分含量0.020%
建议注射量40 到 60%
料筒后部温度271 到 293°c
料筒中部温度282 到 304°c
料筒前部温度293 到 316°c
射嘴温度288 到 310°c
加工（熔体）温度293 到 316°c
模具温度71.1 到 93.3°c
背压0.345 到 0.689mpa
螺杆转速40 到 70rpm
排气孔深度0.025 到 0.076mm
PC 基础创新塑料 945NC