产品说明：
lexan 905 resin is a high flow, opaque, flame retardantpolycarbonate resin blend. it is designed with non-chlorinated,non-brominated fr systems with ul-94 listing of both v0 and 5vratings. its excellent processability, combined with good impact,heat and all opaque colors for aesthetics makes it an excellentcandidate for thin wall applications.
物性信息：
| 比重 | 1.19 g/cc | 1.19 g/cc | astm d792 |
| 密度 | 1.19 g/cc | 0.0430 lb/in³ | iso 1183 |
| 水分吸收 | 0.0700 % | 0.0700 % | 23°c / 50% rh; iso 62 |
| 饱和吸水率 | 0.26 % | 0.26 % | iso 62 |
| 线性成型收缩率,flow | 0.0060 - 0.0080 cm/cm @thickness 3.20 mm | 0.0060 - 0.0080 in/in @thickness 0.126 in | sabic method |
| 线性成型收缩率，横向 | 0.0060 - 0.0080 cm/cm @thickness 3.20 mm | 0.0060 - 0.0080 in/in @thickness 0.126 in | sabic method |
| 熔体流动速率 | 30 g/10 min @load 1.20 kg, temperature 300 °c | 30 g/10 min @load 2.65 lb, temperature 572 °f | astm d1238 |
| 化合物熔体指数 | 29 g/10 min @load 1.20 kg, temperature 300 °c | 29 g/10 min @load 2.65 lb, temperature 572 °f | mvr [cm^3/10 min]; iso 1133 |
| 抗张强度(断裂) | 50.0 mpa | 7250 psi | 50 mm/min; iso 527 |
| 51.0 mpa | 7400 psi | type i, 50 mm/min; astm d638 | |
| 抗张强度(屈服) | 55.0 mpa | 7980 psi | 50 mm/min; iso 527 |
| 56.0 mpa | 8120 psi | type i, 50 mm/min; astm d638 | |
| 伸长率 (断裂) | 97 % | 97 % | 50 mm/min; iso 527 |
| 102 % | 102 % | type i, 50 mm/min; astm d638 | |
| 屈服伸长率 | 5.7 % | 5.7 % | type i, 50 mm/min; astm d638 |
| 5.7 % | 5.7 % | 50 mm/min; iso 527 | |
| 拉伸模量 | 2.20 gpa | 319 ksi | 1 mm/min; iso 527 |
| 2.25 gpa | 326 ksi | 50 mm/min; astm d638 | |
| 弯曲强度 | 92.0 mpa | 13300 psi | 2 mm/min; iso 178 |
| 93.0 mpa | 13500 psi | 1.3 mm/min, 50 mm span; astm d790 | |
| 弯曲模量 | 2.15 gpa | 312 ksi | 1.3 mm/min, 50 mm span; astm d790 |
| 2.30 gpa | 334 ksi | 2 mm/min; iso 178 | |
| 悬壁梁缺口冲击强度 | 7.40 j/cm | 13.9 ft-lb/in | astm d256 |
| 2.30 j/cm @temperature -30.0 °c | 4.31 ft-lb/in @temperature -22.0 °f | astm d256 | |
| 悬壁梁无缺口冲击强度 | 21.5 j/cm | 40.3 ft-lb/in | astm d4812 |
| 20.0 j/cm @temperature -30.0 °c | 37.5 ft-lb/in @temperature -22.0 °f | astm d4812 | |
| 悬壁梁缺口冲击强度 | 58.0 kj/m² | 27.6 ft-lb/in² | 80*10*3; iso 180/1a |
| 21.0 kj/m² @temperature -30.0 °c | 9.99 ft-lb/in² @temperature -22.0 °f | 80*10*3; iso 180/1a | |
| 悬壁梁无缺口冲击强度 | 184 kj/m² | 87.6 ft-lb/in² | 80*10*3; iso 180/1u |
| 183 kj/m² @temperature -30.0 °c | 87.1 ft-lb/in² @temperature -22.0 °f | 80*10*3; iso 180/1u | |
| 简支梁无缺口冲击强度 | 13.5 j/cm² | 64.2 ft-lb/in² | edgew 80*10*3 sp=62mm; iso 179/1eu |
| 13.4 j/cm² @temperature -30.0 °c | 63.8 ft-lb/in² @temperature -22.0 °f | edgew 80*10*3 sp=62mm; iso 179/1eu | |
| 简支梁缺口冲击强度 | 5.00 j/cm² | 23.8 ft-lb/in² | edgew 80*10*3 sp=62mm; iso 179/1ea |
| 1.60 j/cm² @temperature -30.0 °c | 7.61 ft-lb/in² @temperature -22.0 °f | edgew 80*10*3 sp=62mm; iso 179/1ea | |
| 落锤总能量 | 69.0 j @temperature 23.0 °c | 50.9 ft-lb @temperature 73.4 °f | astm d3763 |
| 体积电阻率 | 1.00e+15 - 1.00e+16 ohm-cm | 1.00e+15 - 1.00e+16 ohm-cm | astm d257 |
| 表面电阻 | 1.00e+15 - 1.00e+16 ohm | 1.00e+15 - 1.00e+16 ohm | astm d257 |
| 相比耐漏电起痕指数(cti) | 175 - 250 v | 175 - 250 v | ul 746a |
| 线形热膨胀系数 - 流动 | 69.0 µm/m-°c @temperature -40.0 - 40.0 °c | 38.3 µin/in-°f @temperature -40.0 - 104 °f | astm e 831 |
| 70.0 µm/m-°c @temperature 23.0 - 80.0 °c | 38.9 µin/in-°f @temperature 73.4 - 176 °f | iso 11359-2 | |
| 线性热膨胀系数,横向流动 | 69.0 µm/m-°c @temperature 23.0 - 80.0 °c | 38.3 µin/in-°f @temperature 73.4 - 176 °f | iso 11359-2 |
| 71.0 µm/m-°c @temperature -40.0 - 40.0 °c | 39.4 µin/in-°f @temperature -40.0 - 104 °f | astm e 831 | |
| 载荷下热变形温度(0.46 mpa) | 131 °c | 268 °f | edgew 120*10*4 sp=100mm; iso 75/be |
| 130 °c @thickness 3.20 mm | 266 °f @thickness 0.126 in | unannealed; astm d648 | |
| 载荷下热变形温度(1.8 mpa) | 119 °c | 246 °f | edgew 120*10*4 sp=100mm; iso 75/ae |
| 118 °c @thickness 3.20 mm | 244 °f @thickness 0.126 in | unannealed; astm d648 | |
| 维卡软化温度 | 136 °c | 277 °f | rate b/50; astm d1525 |
| 137 °c | 279 °f | rate b/50; iso 306 | |
| 138 °c | 280 °f | rate b/120; iso 306 | |
| 可燃性(ul94) | v-1 @thickness 0.750 mm | v-1 @thickness 0.0295 in | ul 94 |
| v-0 @thickness 1.10 mm | v-0 @thickness 0.0433 in | ul 94 | |
| 5vb @thickness 2.00 mm | 5vb @thickness 0.0787 in | ul 94 | |
| 5va @thickness 2.80 mm | 5va @thickness 0.110 in | ul 94 | |
| 灼热丝试验 | 875 °c | 1610 °f | iec 60695-2-13 |
| 960 °c @thickness 2.00 mm | 1760 °f @thickness 0.0787 in | iec 60695-2-12 |
| 球压试验，125°c+/-2℃ | pass | iec 60695-10-2 |
展开全文