原包日本宝理40%玻矿lcp laperos e463i
density | 1.72 | g/cm³ | iso 1183 |
molding shrinkage 3 | internal method | ||
across flow : 1.00 mm | 0.50 | % | |
flow : 1.00 mm | 0.090 | ||
water absorption (24 hr, 23°c) | 0.020 | iso 62 | |
hardness | nominal value | unit | test method |
rockwell hardness (m-scale) | 45 | iso 2039-2 |
mechanical | nominal value | ||
tensile strength | 110 | mpa | astm d638 |
tensile elongation (break) | 3.0 | astm d638 | |
flexural modulus | 10600 | iso 178 | |
flexural stress | 130 | iso 178 | |
flexural strain | 3.1 | iso 178 | |
impact | nominal value | ||
charpy notched impact strength (23°c) | 5.0 | kj/m² | iso 179/1ea |
thermal | nominal value | ||
heat deflection temperature | |||
0.45 mpa, unannealed | 270 | °c | iso 75-2/b |
1.8 mpa, unannealed | 235 | iso 75-2/a |
electrical | nominal value | ||
volume resistivity | 1.0e+16 | ohms·cm | iec 60093 |
electric strength | iec 60243-1 | ||
1.00 mm | 44 | kv/mm | |
3.00 mm | 22 | ||
relative permittivity | iec 60250 | ||
1 khz | 4.50 | ||
1 mhz | 3.90 | ||
dissipation factor | 0.030 | ||
arc resistance | 182 | sec | astm d495 |
comparative tracking index | 200 | v | iec 60112 |
flammability | nominal value | ||
flame rating | v-0 | ul 94 |
lcp还可以做印刷电路板、人造卫星电子部件、喷气发动机零件;用于电子电气和汽车机械零件或部件;还可以用于医疗方面。4)lcp塑胶原料可以加入高填充剂作为集成电路封装材料,以代替环氧树脂作线圈骨架的封装材料;作光纤电缆接头护套和高强度元件;代替陶瓷作化工用分离塔中的填充材料等。5)lcp塑胶原料还可以与聚砜、pbt、聚酰胺等塑料共混制成合金,制件成型后其机械强度高,用以代替玻璃纤维增强的聚砜等塑料,既可提高机械强度性能,又可提高使用强度及化学稳定性等。目前正在研究将lcp用于宇航器外部的面板、汽车外装的制动系统等。