索尔维30%玻纤增强lcp xydar g-930
density / specific gravity | 1.60 | g/cm³ | astm d792 |
water absorption (24 hr) | <0.10 | % | astm d570 |
| mechanical | nominal value | unit | test method |
tensile modulus | 15900 | mpa | astm d638 |
tensile strength | 135 | astm d638 | |
tensile elongation (break) | 1.6 | astm d638 | |
flexural modulus | 13400 | astm d790 | |
flexural strength | 172 | astm d790 | |
| impact | nominal value | ||
notched izod impact | 96 | j/m | astm d256 |
unnotched izod impact | 430 | astm d4812 |
| thermal | nominal value | ||
deflection temperature under load | |||
0.45 mpa, unannealed | 301 | °c | astm d648 |
0.45 mpa, unannealed | 305 | iso 75-2/b | |
1.8 mpa, unannealed | 274 | astm d648 | |
1.8 mpa, unannealed | 282 | iso 75-2/a | |
ball pressure test 3 (270°c,3.00 mm) | pass | iec 60695-10-2 | |
clte | astm d696 | ||
flow | 3.6e-6 to 7.2e-6 | cm/cm/°c | |
transverse | 4.0e-5 to 7.9e-5 | ||
rti elec (0.75 mm) | 220 | ul 746 | |
rti imp (0.75 mm) | 200 | ul 746 | |
rti str (0.75 mm) | ul 746 |
| electrical | nominal value | ||
volume resistivity | 1.0e+16 | ohms·cm | astm d257 |
dielectric strength (1.57 mm) | 39 | kv/mm | astm d149 |
热致性lcp具有全芳香族聚酯和共聚酯结构。它还具有密集排列的直链聚合物链结构，形成的产品具有良好的单向机械性能特点。良好高温性能（热变形温度为121～355℃）、良好的抗辐射性、抗水解性、耐候性、耐化学药品性、固有的阻燃性、低发烟性、高尺寸稳定性、低吸湿性、极低的线膨胀系数、高冲击强度和刚性（按相同重量比较，lcp的强度大于钢，但刚性只是钢的15%）。lcp可以耐酸、溶剂和烃类等化学品，并有较好的阻隔性。