SABIC基础创新塑料Cycolac ABS MG37EP

physical properties

物理性质

metric公制数据

english英制数据

comments测试方法

specific gravity 密度

1.05 g/cc

1.05 g/cc

astm d 792

viscosity test粘度 

217000 cp
@temperature 240 °c

217000 cp
@temperature 464 °f

melt; 1000 sec-1; astm d 3825

linear mold shrinkage, flow 线性收缩率/流动

0.0040 - 0.0060 cm/cm
@thickness 3.20 mm

0.0040 - 0.0060 in/in
@thickness 0.126 in

sabic method

melt flow 熔体流动速率

6.6 g/10min
@load 3.80 kg,
temperature 230 °c

6.6 g/10min
@load 8.38 lb,
temperature 446 °f

astm d 1238

22 g/10min
@load 10.0 kg,
temperature 220 °c

22 g/10min
@load 22.0 lb,
temperature 428 °f

iso 1133

mechanical properties力学性能

hardness, rockwell r 罗氏硬度r

106

106

astm d 785

tensile strength at break 断裂拉伸强度

36.0 mpa

5220 psi

5 mm/min; iso 527

tensile strength, yield 屈服拉伸强度

44.0 mpa

6380 psi

type i, 5 mm/min; astm d 638

48.0 mpa

6960 psi

elongation at break 断裂伸长率

18.2 %

18.2 %

5 mm/min; iso 527