SABIC沙伯基础ABS MG37EPX 电镀ABS

physicalproperties物理性质

metric公制数据

english英制数据

comments测试方法

specificgravity 密度

1.05 g/cc

1.05 g/cc

astm d792

density比重 

1.04 g/cc

0.0376 lb/in³

iso1183

viscositytest粘度 

217000 cp
@temperature 240 °c

217000 cp
@temperature 464 °f

melt;1000 sec-1; astm d 3825

linearmold shrinkage, flow 线性收缩率/流动

0.0040 - 0.0060 cm/cm
@thickness 3.20 mm

0.0040 - 0.0060 in/in
@thickness 0.126 in

sabicmethod

meltflow 熔体流动速率

6.6 g/10min
@load3.80 kg,
temperature230 °c

6.6 g/10min
@load8.38 lb,
temperature446 °f

astm d1238

22 g/10min
@load10.0 kg,
temperature220 °c

22 g/10min
@load22.0 lb,
temperature428 °f

iso1133

mechanicalproperties力学性能

hardness,rockwell r 罗氏硬度r

106

astm d785

tensilestrength at break 断裂拉伸强度

36.0 mpa

5220 psi

5 mm/min;iso 527

tensilestrength, yield 屈服拉伸强度

44.0 mpa

6380 psi

type i, 5mm/min; astm d 638

48.0 mpa

6960 psi

elongation at break 断裂伸长率

18.2%

54 %

54 %

elongation at yield 屈服伸长率

2.0 %

tensilemodulus 拉伸模量

2.47 gpa

358 ksi

5 mm/min;astm d 638

2.72 gpa

395 ksi

1 mm/min;iso 527

flexuralyield strength 弯曲屈服强度

73.0 mpa

10600 psi

2 mm/min;iso 178

90.0 mpa

13100 psi

1.3mm/min, 50 mm span; astm d 790

flexuralmodulus 弯曲弹性模量

2.81 gpa

408 ksi

izodimpact, notched悬臂梁缺口冲击强度 

0.880 j/cm
@temperature -40.0 °c

1.65 ft-lb/in
@temperature -40.0 °f

astm d256

2.50 j/cm
@temperature 23.0 °c

4.68 ft-lb/in
@temperature 73.4 °f

izodimpact, notched 悬臂梁缺口冲击强度(iso) 

6.00 kj/m²
@temperature -40.0 °c

2.86 ft-lb/in²
@temperature -40.0 °f

80*10*4;iso 180/1a

8.00 kj/m²
@temperature -30.0 °c

3.81 ft-lb/in²
@temperature -22.0 °f

23.0 kj/m²
@temperature 23.0 °c

10.9 ft-lb/in²
@temperature 73.4 °f

impacttest冲击试验数据 

35.0 j
@temperature 23.0 °c

25.8 ft-lb
@temperature 73.4 °f

instrumented impact total energy; astm d 3763

thermalproperties热性能

cte,linear, parallel to flow 线性热膨胀系数

60.0 µm/m-°c
@temperature -40.0 - 40.0 °c

33.3 µin/in-°f
@temperature -40.0 - 104 °f

iso11359-2

cte,linear, transverse to flow 线性热膨胀系数/横向

deflection temperature at热变形温度 0.46 mpa (66 psi) 

88.0 °c
@thickness 3.20 mm

190 °f
@thickness 0.126 in

unannealed; astm d 648

deflection temperature at热变形温度 1.8 mpa (264 psi) 

82.0 °c

180 °f

flatw80*10*4 sp=64mm; iso 75/af

76.0 °c
@thickness 3.20 mm

169 °f
@thickness 0.126 in

vicatsoftening point 维卡软化点

94.0 °c

201 °f

rateb/50; iso 306