lnp* stat-kon* compound
lnp stat-kon resin all series
lnp* stat-kon* composites contain electrically conductiveadditives. they and span a broad range of surface resistivity andelectrical activity, from antistatic, through conductive, toelectromagnetic interference (emi) shielding. stat-kon* compositesoffer cost-effective solutions when products must avoid staticelectricity buildup or discharge. lnp specialty compound offeringsare available in a broad portfolio of standard and engineeringmaterials.
lnp™ stat-kon™ compound pesjx89626 塑料物性表
lnp* stat-kon* jx89626 is a compound based on polyethersulfone(pes) containing proprietary fillers. characteristics of this gradeare electrically conductive.
| mechanical | value | unit | standard |
| tensilestress,brk,type i,5mm/min | 1660 | kgf/cm² | astm d638 |
| tensilestrain,brk,type i,5mm/min | 2.1 | % | astm d638 |
| tensilemodulus,50mm/min | 121700 | kgf/cm² | astm d638 |
| flexuralstress,brk,1.3mm/min,50mm span | 2420 | kgf/cm² | astm d790 |
| flexuralmodulus,1.3mm/min,50mm span | 102900 | kgf/cm² | astm d790 |
| tensilestress,break,5mm/min | 161 | mpa | iso 527 |
| tensilestrain,break,5mm/min | 2.2 | % | iso 527 |
| tensilemodulus,1mm/min | 11160 | mpa | iso 527 |
| flexuralstress | 226 | mpa | iso 178 |
| flexuralmodulus,2mm/min | 9670 | mpa | iso 178 |
| impact | value | unit | standard |
| izodimpact,unnotched,23℃ | 60 | cm-kgf/cm | astm d4812 |
| izodimpact,notched,23℃ | 5 | cm-kgf/cm | astm d256 |
| multiaxialimpact | 38 | cm-kgf | iso 6603 |
| instrumentedimpact total energy,23℃ | 74 | cm-kgf | astm d3763 |
| izodimpact,unnotched 80*10*4 +23℃ | 36 | kj/m² | iso180/1u |
| izodimpact,notched 80*10*4 +23℃ | 6 | kj/m² | iso180/1a |
| thermal | value | unit | standard |
| hdt,0.45mpa,3.2mm,unannealed | 220 | ℃ | astm d648 |
| hdt,1.82mpa,3.2mm,unannealed | 214 | ℃ | astm d648 |
| cte,-30℃ to30℃,flow | 4.70e-05 | 1/℃ | astm d696 |
| cte,-30℃ to30℃,xflow | 3.80e-05 | 1/℃ | astm d696 |
| hdt/bf,0.45mpa flatw 80*10*4 sp=64mm | 219 | ℃ | iso75/bf |
| hdt/af,1.8mpa flatw 80*10*4 sp=64mm | 214 | ℃ | iso75/af |
| physical | value | unit | standard |
| specificgravity | 1.41 | - | astm d792 |
| density | 1.41 | g/cm³ | astm d792 |
| moistureabsorption,50% rh,24 hrs | 0.49 | % | astm d570 |
| moldshrinkage,flow,24 hrs(5) | 0.1-0.3 | % | astm d955 |
| moldshrinkage,xflow,24 hrs(5) | 0.5-0.8 | % | astm d955 |
| moistureabsorption(23℃/50% rh) | 0.71 | % | iso 62 |
| electrical | value | unit | standard |
| surfaceresistivity | 2.e+00-5.e+00 | ohm | astm d257 |
| sourcegmd,last updated:2010/05/24 | |||
| parameterinjection molding | value | unit |
| dryingtemperature | 120-150 | ℃ |
| dryingtime | 4 | hrs |
| maximummoisture content | 0.05 | % |
| melttemperature | 355-370 | ℃ |
| front-zone 3temperature | 370-380 | ℃ |
| middle-zone 2temperature | 360-370 | ℃ |
| rear-zone 1temperature | 345-355 | ℃ |
| moldtemperature | 140-150 | ℃ |
| backpressure | 0.3-0.7 | mpa |
| screwspeed | 60-100 | rpm |
| sourcegmd,last updated:2010/05/24 | ||