dupontperformance polymers minlon® 10b140 bk061 nylon 66 (unverifieddata)

polymer,thermoplastic,nylon,nylon 66,nylon 66, 40% mineralfilleddupont performance polymers

dupont performance polymers minlon® 10b140 bk061 nylon 66(unverified data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.50 g/cc0.0542 lb/in³dam; iso 1183填料含量40 %40 %damwater absorption1.6 %

@temperature 23.0 °c

1.6 %

@temperature 73.4 °f

e 50%rh; dam; iso 62, similar to
5.0 %

@temperature 23.0 °c

5.0 %

@temperature 73.4 °f

saturation, immersed; dam; iso 62, similar to机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)54.0 mpa

@temperature 23.0 °c

7830 psi

@temperature 73.4 °f

50%rh; iso 527
82.0 mpa

@temperature 23.0 °c

11900 psi

@temperature 73.4 °f

dam; iso 527伸长率 (断裂)3.5 %

@temperature 23.0 °c

3.5 %

@temperature 73.4 °f

dam; iso 527
9.0 %

@temperature 23.0 °c

9.0 %

@temperature 73.4 °f

50%rh; iso 527拉伸模量3.80 gpa

@temperature 23.0 °c

551 ksi

@temperature 73.4 °f

50%rh; iso 527
6.60 gpa

@temperature 23.0 °c

957 ksi

@temperature 73.4 °f

dam; iso 527悬壁梁缺口冲击强度3.50 kj/m²

@temperature 23.0 °c

1.67 ft-lb/in²

@temperature 73.4 °f

dam; iso 180/1a
4.00 kj/m²

@temperature 23.0 °c

1.90 ft-lb/in²

@temperature 73.4 °f

50%rh; iso 180/1a简支梁无缺口冲击强度3.50 j/cm²

@temperature 23.0 °c

16.7 ft-lb/in²

@temperature 73.4 °f

dam; iso 179/1eu
6.00 j/cm²

@temperature 23.0 °c

28.6 ft-lb/in²

@temperature 73.4 °f

50%rh; iso 179/1eu简支梁缺口冲击强度0.350 j/cm²

@temperature 23.0 °c

dam; iso 179/1ea
0.450 j/cm²

@temperature 23.0 °c

2.14 ft-lb/in²

@temperature 73.4 °f

50%rh; iso 179/1ea电气性能额定值 (公制)额定值 (英制)测试方法相比耐漏电起痕指数(cti)>= 600 v

@temperature 23.0 °c

>= 600 v

@temperature 73.4 °f

dam; ul 746a热性能额定值 (公制)额定值 (英制)测试方法熔融温度263 °c505 °f10°c/min; dam; iso 11357-1/-3载荷下热变形温度(0.46 mpa)240 °c464 °fdam; iso 75-1/-2载荷下热变形温度(1.8 mpa)170 °c338 °fdam; iso 75-1/-2ul rti105 °c

@thickness 0.710 mm

221 °f

@thickness 0.0280 in

dam; ul 746b
120 °c

@thickness 3.00 mm

248 °f

@thickness 0.118 in

dam; ul 746b
120 °c

@thickness 1.50 mm

248 °f

@thickness 0.0591 in

dam; ul 746bul rti，机械冲击65.0 °c

@thickness 0.710 mm

149 °f

@thickness 0.0280 in

dam; ul 746b
105 °c

@thickness 1.50 mm

221 °f

@thickness 0.0591 in

dam; ul 746b
115 °c

@thickness 3.00 mm

239 °f

@thickness 0.118 in

dam; ul 746bul rti，机械无冲击65.0 °c

@thickness 0.710 mm

dam; ul 746b
115 °c

@thickness 1.50 mm

239 °f

@thickness 0.0591 in

dam; ul 746b可燃性(ul94)hb

@thickness 1.50 mm

hb

@thickness 0.0591 in

dam; ul94
hb

@thickness 0.710 mm

hb

@thickness 0.0280 in

dam; ul94
hb

@thickness 3.00 mm

hb

@thickness 0.118 in

dam; iec 60695-11-10
hb

@thickness 1.50 mm

dam; iec 60695-11-10
hb

@thickness 0.710 mm

dam; iec 60695-11-10加工性能额定值 (公制)额定值 (英制)测试方法加工（熔体）温度285 - 305 °c545 - 581 °fdam
295 °c563 °fdam; optimum模具温度70.0 - 120 °c158 - 248 °fdam
100 °c212 °fdam; optimum干燥温度80.0 °c176 °fdam干燥时间2.00 - 4.00 hour2.00 - 4.00 hourdam水分含量<= 0.20 %<= 0.20 %dam材料描述
测试方法外观black colordamdrying recommendedyes, if moisture content of resin exceeds recommended leveldamfillermineral fillerdam形式pelletsdamgenericnylon 66dammaterial statuscurrentdam部件标识代码>pa66-md40<iso 11469; dampolymer familypolyamidedampolymer typepa66dam加工方法injection moldingdam产品分类low warp resinsdam
mineral reinforced resinsdam
mineral reinforced resinsdam树脂识别pa66-md40iso 1043; dam符合rohs指令contact manufacturerdam