PA66 A3EG10 PA66 A3EG10

basf pa66 ultramid a3eg10物性参数物性表

以下是basf pa66 ultramid a3eg10中英文物性表

basf ultramid® a3eg10pa66(尼龙66-聚酰胺)

the property table is providedby www.plas-cn.com, welcome to download, reprintplease indicate the source!

physical properties物理性质

metric公制数据

english英制数据

comments测试方法

bulk density密度 

0.500 - 0.800 g/cc

0.0181 - 0.0289 lb/in³

density密度 

1.56 g/cc

0.0564 lb/in³

iso 1183

water absorption吸水率 

3.7 - 4.3 %

saturation; iso 62

moisture absorption ate吸湿平衡 

1.0 - 1.4 %

23°c; 50% rh; iso 62

viscosity measurement粘度 

130

iso 307

linear mold shrinkage 线性收缩率

0.0045 cm/cm

0.0045 in/in

restricted

linear mold shrinkage,flow线性收缩率/流动 

0.0033 cm/cm

0.0033 in/in

iso 2577

0.0045 cm/cm

0.0045 in/in

tm=300°c, tw=80°c

linear mold shrinkage,transverse线性收缩率/横向 

0.0082 cm/cm

0.0082 in/in

iso 2577

melt flow熔体流动速率 

31.2 g/10min
@load 5.00kg,
temperature 275 °c

31.2 g/10min
@load 11.0lb,
temperature 527 °f

iso 1133

mechanical properties力学性能

tensile strength,yield屈服拉伸强度 

240 mpa

34800 psi

50 mm/min; iso 527-1/-2

elongation at yield屈服伸长率 

2.5 %

50 mm/min; iso 527-1/-2

modulus of elasticity弹性模量 

16.8 gpa

2440 ksi

iso 527-1/-2

flexural strength弯曲强度 

360 mpa

52200 psi

at max force; iso 178

flexural modulus弯曲弹性模量 

15.0 gpa

2180 ksi

iso 178

izod impact,notched悬臂梁缺口冲击强度 (iso) 

13.0 kj/m²
@temperature23.0 °c

6.19 ft-lb/in²
@temperature73.4 °f

iso 180/a

charpy impactunnotched夏比缺口试样冲击 

9.00 j/cm²
@temperature-30.0 °c

42.8 ft-lb/in²
@temperature-22.0 °f

iso 179/1eu

9.50 j/cm²
@temperature23.0 °c

45.2 ft-lb/in²
@temperature73.4 °f

charpy impact, notched夏比缺口冲击 

1.30 j/cm²
@temperature-30.0 °c

6.19 ft-lb/in²
@temperature-22.0 °f

iso 179/1ea

1.80 j/cm²
@temperature23.0 °c

8.57 ft-lb/in²
@temperature73.4 °f

electrical properties电性能

volume resistivity体积电阻率 

1.00e+13 ohm-cm

iec 60093

dielectric constant 介电常数

3.8
@frequency 1.00hz

iec 60250

dissipation factor 耗散因数

0.015
@frequency 1.00e+6hz

iec 60250

comparative trackingindex 跟踪指数

550 v

test solution a; iec 60112

thermal properties热性能

cte, linear, parallel toflow线性热膨胀系数 

0.0500 - 0.200 µm/m-°c
@temperature 23.0 - 80.0 °c

0.0278 - 0.111 µin/in-°f
@temperature 73.4 - 176 °f

din 11359-1/-2

cte, linear, transverse toflow线性热膨胀系数/横向 

0.500 - 0.600 µm/m-°c
@temperature 23.0 - 80.0 °c

0.278 - 0.333 µin/in-°f
@temperature 73.4 - 176 °f

din 11359-1/-2

specific heat capacity比热容 

1.30 j/g-°c

0.311 btu/lb-°f

thermal conductivity导热系数 

0.370 w/m-k

2.57 btu-in/hr-ft²-°f

din 52612

melting point熔点 

260 °c

500 °f

din 53765

maximum service temperature,air使用温度 

240 °c

464 °f

deflection temperatureat热变形温度0.46 mpa (66 psi) 

250 °c

482 °f

iso 75-1/-2

deflection temperatureat热变形温度1.8 mpa (264 psi) 

250 °c

482 °f

iso 75-1/-2

decompositiontemperature分解温度 

>= 310 °c

>= 590 °f

flammability, ul94阻燃等级 

hb
@thickness 1.60mm

hb
@thickness 0.0630in

processing properties加工性能

processing temperature加工温度 

80.0 °c

176 °f

hopper throat

zone 1  1区

300 °c

572 °f

feed zone

zone 2  2区

300 °c

572 °f

compression

zone 3  3区

metering-zone

zone 4  4区

nozzle

melt temperature熔体温度 

290 - 310 °c

554 - 590 °f

injection-molding/extrusion

300 °c

optimal

mold temperature模具温度 

optimal

80.0 - 90.0 °c

176 - 194 °f

injection-molding

drying temperature干燥温度 

80.0 °c

176 °f

dry time干燥温度 

4 hour

moisture content水分含量 

0.030 - 0.060 %

<= 0.15 %

<= 0.15 %