q/bqb 310－2018 4 表 2 型号 成分 a（摩尔质量） ％ c si mn p s alt saph310≤0.10 ≤0.30 ≤0.80 ≤0.025 ≤0.020 ≥0.010 saph370 ≤0.21 ≤0.30 ≤1.00saph400 ≤0.21 ≤0.30 ≤1.40 ≤0.025 ≤0.020 saph440 ≤1.60 spfh540 ≤0.15≤0.50 ≤1.80 spfh590 ≤0.18 ≤0.60 ≤2.00 ≤0.025 ≤0.020 spfh780 ≤0.20≤1.00 ≤2.10 b440qk ≤0.21 ≤0.35 ≤1.80 ≤0.025 ≤0.020 b330cl ≤0.10≤0.30 ≤0.80 b380cl ≤0.12 ≤0.30 ≤1.50 ≤0.025 ≤0.020 b420cl ≤0.12≤0.30 ≤1.50 b450cl ≤0.10 ≤0.30 ≤1.50 ≤0.025 ≤0.020 b500cl ≤0.12≤0.30 ≤1.60 ≤0.025 ≤0.020 b530cl ≤0.12 ≤0.30 ≤1.60 ≤0.025 ≤0.020b550cl ≤0.12 ≤0.30 ≤2.00 ≤0.025 ≤0.020 b600cl ≤0.15 ≤0.30 ≤2.00≤0.025 ≤0.020 b650cl ≤0.15 ≤0.50 ≤2.00 ≤0.025 ≤0.020 b320l ≤0.10≤0.30 ≤0.80 ≤0.025 ≤0.020 b420l ≤0.12 ≤0.50 ≤1.50 ≤0.020 b510l≤0.16 ≤0.50 ≤1.60 ≤0.020 b510dl ≤0.18 ≤0.30 ≤1.60 ≤0.025 ≤0.020b550l ≤0.16 ≤0.50 ≤1.60 ≤0.025 ≤0.020 b440qzr ≤0.12 ≤0.50 ≤1.30≤0.025 ≤0.020 － b480qzr ≤0.16 ≤0.50 ≤1.50 ≤0.020 a为改进钢的特性，依据必须可加上别的铝合金原素，这时 alt 的低限不规定。 表 3 型号 成分 a（摩尔质量） ％ c si mn ps alt 别的 ≤0.12 ≤0.50 ≤1.30 ≤0.025 ≤0.020 ≥0.015 nb≤0.09v≤0.20 ti≤0.15 ≤1.40 ≤1.50 ≤1.60 ≤1.70 a 为改进钢的特性，依据必须可加上 nb、v、ti 中一种或几类铝合金原素，但 nb vti≤0.22%。 q/bqb 310－2018 5 表 4 型号 成分 a （摩尔质量） ％ c mn si p s alt nbav a tia mo b b610l(b600l) ≤0.12 ≤1.80 ≤0.50 ≤0.025 ≤0.015≥0.015 ≤0.09 ≤0.20 ≤0.15 － － b650l ≤0.12 ≤1.90 ≤0.50≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50 ≤0.005 b700l≤0.12 ≤2.00 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09 ≤0.20 ≤0.22 ≤0.50≤0.005 b750l ≤0.12 ≤2.10 ≤0.60 ≤0.025 ≤0.015 ≥0.015 ≤0.09≤0.20 ≤0.22 ≤0.50 ≤0.005 a 钢中可加上 nb、v、ti 中一种或几类铝合金原素，但 nb vti≤0.22。 6.5 结构力学和使用性能 6.5.1 厚钢板及钢链的结构力学和使用性能应合乎相对表 5～表 10 的要求。6.5.2 弯折实验后，试件的外表层不可有人眼由此可见的裂痕。供货方如能确保弯折实验达标，