PC 德国科思创(拜耳)6555 德国拜耳 6555

pc 德国科思创(拜耳)6555 德国拜耳 6555

pc德国科思创6555物性表

规格级别其它 其它 注塑外观颜色
该料用途用于工业产品及电子电器备注说明特性：中高粘度，完全阻燃v-0/3.0mm，注塑式挤塑
性能项目试验条件[状态]测试方法测试数据数据单位物理性能密度(23°c)
iso11831.20g/cm³表观密度2
iso600.64g/cm³熔流率（熔体流动速率）(300°c/1.2kg)
iso113310g/10min溶化体积流率（mvr）(300°c/1.2kg)
iso113310.0cm³/10min收缩率横向流量iso25770.60to0.80%流量iso25770.60to0.80%横向流量:2.00mm3iso294-40.75%流量:2.00mm3iso294-40.70%吸水率(饱和,23°c)
iso620.30%吸水率(平衡,23°c,50%rh)
iso620.12%机械性能拉伸模量(23°c)
iso527-2/12400mpa拉伸应力(屈服,23°c)
iso527-2/5066.0mpa拉伸应力(断裂,23°c)
iso527-2/5070.0mpa拉伸应变(屈服,23°c)
iso527-2/506.2%拉伸应变(断裂,23°c)
iso527-2/50130%标称拉伸断裂应变(23°c)
iso527-2/50>50%tensilecreepmodulus(1hr)
iso899-12200mpa拉伸蠕变模量(1000hr)
iso899-11900mpa弯曲模量4(23°c)
iso1782400mpa弯曲应力43.5%strain,23°ciso17874.0mpa23°ciso17898.0mpaflexuralstrainatflexuralstrength5(23°c)
iso1787.1%薄膜watervaportransmissionrate(23°c,85%rh,100µm)
iso15106-115g/m²/24hrgaspermeationcarbondioxide:23°c,25.4µmiso255616900cm³/m²/bar/24hrcarbondioxide:23°c,100.0µmiso25564300cm³/m²/bar/24hrnitrogen:23°c,25.4µmiso2556510cm³/m²/bar/24hrnitrogen:23°c,100.0µmiso2556130cm³/m²/bar/24hroxygen:23°c,25.4µmiso25562760cm³/m²/bar/24hroxygen:23°c,100.0µmiso2556700cm³/m²/bar/24hr冲击性能简支梁缺口冲击强度6-30°c,完全断裂iso739114kj/m²23°c,局部断裂iso739170kj/m²简支梁无缺口冲击强度-60°ciso179/1eunobreak
-30°ciso179/1eunobreak
23°ciso179/1eunobreak
悬壁梁缺口冲击强度7-30°c,完全断裂iso739112kj/m²23°c,局部断裂iso739165kj/m²多轴向仪器化冲击能量-30°ciso6603-265.0j23°ciso6603-260.0j多轴向仪器化冲击力峰值-30°ciso6603-26300n23°ciso6603-25400n硬度球压硬度
iso2039-1115mpa热性能热变形温度(0.45mpa,未退火)
iso75-2/b137°c热变形温度(1.8mpa,未退火)
iso75-2/a125°c玻璃转化温度8
iso11357-2145°c维卡软化温度--iso306/b50144°c--iso306/b120145°cballpressuretest(136°c)
iec60695-10-2pass
线形热膨胀系数-流动(23到55°c)
iso11359-26.5e-5cm/cm/°cclte-transverse(23to55°c)
iso11359-26.5e-5cm/cm/°c导热系数9(23°c)
iso83020.20w/m/krtielec(1.5mm)
ul746125°crtiimp(1.5mm)
ul746115°crtistr(1.5mm)
ul746125°c电气性能表面电阻率
iec600931.0e+16ohms体积电阻率(23°c)
iec600931.0e+16ohms·cm介电强度(23°c,1.00mm)
iec60243-134kv/mm相对电容率23°c,100hziec602503.10
23°c,1mhziec602503.00
耗散因数23°c,100hziec602508.0e-4
23°c,1mhziec602509.0e-3
漏电起痕指数解决方案aiec60112225v解决方案biec60112125v可燃性ul阻燃等级1.0mmul94v-2
3.0mmul94v-0
灼热丝易燃指数0.75mmiec60695-2-12875°c1.5mmiec60695-2-12960°c3.0mmiec60695-2-12960°c热灯丝点火温度0.75mmiec60695-2-13875°c1.5mmiec60695-2-13875°c3.0mmiec60695-2-13875°c极限氧指数10
iso4589-235%applicationofflamefromsmallburner-methodkandf(2.00mm)
din53438-1,-3k1,f1
burningrate-us-fmvss(>1.00mm)
iso3795passed
flashignitiontemperature
astmd1929460°cglowwiretest1.50mmedfhn60e.02750°c3.00mmedfhn60e.02750°c针焰试验methodf:1.50mmiec60695-11-52.0minmethodf:2.00mmiec60695-11-52.0minmethodf:3.00mmiec60695-11-52.0minmethodk:1.50mmiec60695-11-51.0minmethodk:2.00mmiec60695-11-52.0minmethodk:3.00mmiec60695-11-52.0minselfignitiontemperature
astmd1929530°c光学性能refractiveindex11
iso4891.586
透射率1000µmiso13468-289.0%2000µmiso13468-289.0%3000µmiso13468-288.0%4000µmiso13468-287.0%additionalinformation补充信息
testmethodnominalvalueunitelectrolyticalcorrosion(23°c)
iec60426a1
isoshortname
iso7391-pc,mfr,(,,)-09-9