lexan pc 920a物性
低粘度注射成形,阻燃的pc 。特殊的表面外观。有透明和不透明的颜色
property
mechanical
valueunitstandard
tensile stress, yld, type i, 50 mm/min
630
kgf/cm2
astm d 638
tensile stress, brk, type i, 50 mm/min
560
tensile strain, yld, type i, 50 mm/min
7
%
tensile strain, brk, type i, 50 mm/min
90
flexural stress, yld, 1.3 mm/min, 50 mm span
920
astm d 790
flexural modulus, 1.3 mm/min, 50 mm span
22800
hardness, rockwell m
70
-
astm d 785
hardness, rockwell r
118
taber abrasion, cs-17, 1 kg
10
mg/1000cy
astm d 1044
impact
izod impact, unnotched, 23°c
326
cm-kgf/cm
astm d 4812
izod impact, notched, 23°c
65
astm d 256
tensile impact, type "s"
535
cm-kgf/cm2
astm d 1822
falling dart impact (d 3029), 23°c
1728
cm-kgf
astm d 3029
thermal
vicat softening temp, rate b/50
151
°c
astm d 1525
hdt, 0.45 mpa, 6.4 mm, unannealed
137
astm d 648
hdt, 1.82 mpa, 6.4 mm, unannealed
132
cte, -40°c to 95°c, flow
6.84e-05
1/°c
astm e 831
thermal conductivity
0.19
w/m-°c
astm c 177
relative temp index, elec
130
ul 746b
relative temp index, mech w/impact
120
relative temp index, mech w/o impact
physical
specific gravity
1.21
astm d 792
specific volume
0.83
cm2g
density
1.217
g/cm2
water absorption, 24 hours
0.15
astm d 570
water absorption, e, 23c
0.35
water absorption, e, 100°c
0.58
mold shrinkage, flow, 3.2 mm
0.5 - 0.7
sabic method
melt flow rate, 300°c/1.2 kgf
14.5
g/10 min
astm d 1238
optical
light transmission
85
astm d 1003
haze
1
refractive index
1.586
astm d 542
electrical
volume resistivity
>1.e+17
ohm-cm
astm d 257
dielectric strength, in air, 3.2 mm
16.7
kv/mm
astm d 149
relative permittivity, 50/60 hz
3.01
astm d 150
relative permittivity, 1 mhz
2.96
dissipation factor, 50/60 hz
0.0009
dissipation factor, 1 mhz
0.01
arc resistance, tungsten {plc}
plc code
astm d 495
hot wire ignition {plc)
2
ul 746a
high voltage arc track rate {plc}
3
high ampere arc ign, surface {plc}
comparative tracking index (ul) {plc}
flame characteristics
ul recognized, 94v-2 flame class rating (3)
1.47
mm
ul 94
ul recognized, 94v-0 flame class rating (3)
2.99
radiant panel listing
yes
ul tested
processing
parameter
injection molding
valueunit
drying temperature
drying time
3 - 4
hrs
drying time (cumulative)
48
maximum moisture content
0.02
melt temperature
290 - 310
nozzle temperature
280 - 305
front - zone 3 temperature
middle - zone 2 temperature
275 - 300
rear - zone 1 temperature
265 - 290
mold temperature
70 - 95
back pressure
0.3 - 0.7
mpa
screw speed
40 - 70
rpm
shot to cylinder size
40 - 60
vent depth
0.025 - 0.076