性能项目试验条件[状态]测试方法测试数据数据单位物理性能熔融指数200°c/5kgastmd-1238(g)2.2g/10min成型收缩率
astm d-9550.4~0.7%比重
astm d-7921.11
机械性能伸张率(破断点)50mm/minastm d-63840%张力摸数1mm/minastmd-63822200(2180)kg/cm洛氏强度r-scaleastm d-785112
弯曲强度15mm/minastm d-790800(78)kg/cmizod冲击强度1/4",23°castmd-25610(100)kg.cm/cm(j/m)伸张率(抗拒点)50mm/minastmd-638≥6%张力强度50mm/minastm d-638520(51)kg/cm弯曲摸数15mm/minastmd-79025000(2450)kg/cm热性能燃烧性1/8"iec707-mm/min热变形温度4.6kg/cm21/4"annealed(unannealed)astmd-64895(90)℃热变形形温度1.86kgf/cm21/4astmd-64889(89)℃微卡软化点1kg/120℃/h(5kg/50℃/h)astmd-1525100(93)℃燃烧性1/8"ul-94hbclass
ABSTR-558,ABS韩国LG,TR-558