PA66美国杜邦HTN53G60LRHF BN535代理商

dupont performance polymers zytel® htn 53g60lrhf bk083polyphthalamide (ppa) (unverified data**) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.72 g/cc0.0621 lb/in³dam; iso1183线性成型收缩率,flow0.0010 cm/cm0.0010 in/indam; iso 294-42577线性成型收缩率，横向0.0050 cm/cm0.0050 in/indam; iso 294-4 2577机械性能额定值(公制)额定值 (英制)测试方法抗张强度(断裂)225 mpa32600 psi50%rh; iso 527-1/-2
265 mpa38400 psidam; iso 527-1/-2抗张强度4.08 mpa

@strain 0.0600 %, temperature 150 °c

592 psi

@strain 0.0600 %, temperature 302 °f

50%rh; iso 11403-1 -2
4.40 mpa

@strain 0.0600 %, temperature 180 °c

638 psi

@strain 0.0600 %, temperature 356 °f

dam; iso 11403-1 -2
5.17 mpa

@strain 0.0600 %, temperature 150 °c

750 psi

@strain 0.0600 %, temperature 302 °f

dam; iso 11403-1 -2
5.69 mpa

@strain 0.0400 %, temperature 0.000 °c

825 psi

@strain 0.0400 %, temperature 32.0 °f

50%rh; iso 11403-1 -2
5.88 mpa

@strain 0.0500 %, temperature 23.0 °c

853 psi

@strain 0.0500 %, temperature 73.4 °f

dam; iso 11403-1 -2
5.98 mpa

@strain 0.0600 %, temperature 90.0 °c

867 psi

@strain 0.0600 %, temperature 194 °f

50%rh; iso 11403-1 -2
7.13 mpa

@strain 0.0600 %, temperature -20.0 °c

1030 psi

@strain 0.0600 %, temperature -4.00 °f

50%rh; iso 11403-1 -2
7.38 mpa

@strain 0.0500 %, temperature 0.000 °c

1070 psi

@strain 0.0500 %, temperature 32.0 °f

dam; iso 11403-1 -2
7.56 mpa

@strain 0.0500 %, temperature 90.0 °c

1100 psi

@strain 0.0500 %, temperature 194 °f

dam; iso 11403-1 -2
7.63 mpa

@strain 0.0600 %, temperature -20.0 °c

1110 psi

@strain 0.0600 %, temperature -4.00 °f

dam; iso 11403-1 -2
8.40 mpa

@strain 0.0400 %, temperature 40.0 °c

1220 psi

@strain 0.0400 %, temperature 104 °f

50%rh; iso 11403-1 -2
9.24 mpa

@strain 0.0400 %, temperature 23.0 °c

1340 psi

@strain 0.0400 %, temperature 73.4 °f

50%rh; iso 11403-1 -2
10.59 mpa

@strain 0.0400 %, temperature 40.0 °c

1536 psi

@strain 0.0400 %, temperature 104 °f

dam; iso 11403-1 -2
11.75 mpa

@strain 0.200 %, temperature 150 °c

1704 psi

@strain 0.200 %, temperature 302 °f

50%rh; iso 11403-1 -2
12.49 mpa

@strain 0.220 %, temperature 180 °c

1812 psi

@strain 0.220 %, temperature 356 °f

dam; iso 11403-1 -2
15.02 mpa

@strain 0.230 %, temperature 150 °c

2178 psi

@strain 0.230 %, temperature 302 °f

dam; iso 11403-1 -2
17.25 mpa

@strain 0.200 %, temperature 90.0 °c

2502 psi

@strain 0.200 %, temperature 194 °f

50%rh; iso 11403-1 -2
22.5 mpa

@strain 0.210 %, temperature 90.0 °c

3260 psi

@strain 0.210 %, temperature 194 °f

dam; iso 11403-1 -2
25.67 mpa

@strain 0.150 %, temperature 40.0 °c

3723 psi

@strain 0.150 %, temperature 104 °f

50%rh; iso 11403-1 -2
28.51 mpa

@strain 0.140 %, temperature 23.0 °c

4135 psi

@strain 0.140 %, temperature 73.4 °f

50%rh; iso 11403-1 -2
29.52 mpa

@strain 0.130 %, temperature 23.0 °c

4282 psi

@strain 0.130 %, temperature 73.4 °f

dam; iso 11403-1 -2
29.75 mpa

@strain 0.760 %, temperature 150 °c

4315 psi

@strain 0.760 %, temperature 302 °f

50%rh; iso 11403-1 -2
30.63 mpa

@strain 0.800 %, temperature 180 °c

4443 psi

@strain 0.800 %, temperature 356 °f

dam; iso 11403-1 -2
31.13 mpa

@strain 0.150 %, temperature 0.000 °c

4515 psi

@strain 0.150 %, temperature 32.0 °f

dam; iso 11403-1 -2
31.52 mpa

@strain 0.150 %, temperature 0.000 °c

4572 psi

@strain 0.150 %, temperature 32.0 °f

50%rh; iso 11403-1 -2
32.16 mpa

@strain 0.140 %, temperature 40.0 °c

4664 psi

@strain 0.140 %, temperature 104 °f

dam; iso 11403-1 -2
37.36 mpa

@strain 0.170 %, temperature -20.0 °c

5419 psi

@strain 0.170 %, temperature -4.00 °f

50%rh; iso 11403-1 -2
37.9 mpa

@strain 0.240 %, temperature 40.0 °c

5500 psi

@strain 0.240 %, temperature 104 °f

50%rh; iso 11403-1 -2
38.73 mpa

@strain 0.150 %, temperature -20.0 °c

5617 psi

@strain 0.150 %, temperature -4.00 °f

dam; iso 11403-1 -2
40.49 mpa

@strain 0.200 %, temperature 23.0 °c

5873 psi

@strain 0.200 %, temperature 73.4 °f

50%rh; iso 11403-1 -2
40.61 mpa

@strain 1.01 %, temperature 150 °c

5890 psi

@strain 1.01 %, temperature 302 °f

dam; iso 11403-1 -2
40.78 mpa

@strain 1.62 %, temperature 150 °c

5915 psi

@strain 1.62 %, temperature 302 °f

50%rh; iso 11403-1 -2
41.26 mpa

@strain 0.170 %, temperature 23.0 °c

5984 psi

@strain 0.170 %, temperature 73.4 °f

dam; iso 11403-1 -2
41.27 mpa

@strain 1.69 %, temperature 180 °c

5986 psi

@strain 1.69 %, temperature 356 °f

dam; iso 11403-1 -2
43.31 mpa

@strain 0.720 %, temperature 90.0 °c

6282 psi

@strain 0.720 %, temperature 194 °f

50%rh; iso 11403-1 -2
44.86 mpa

@strain 0.200 %, temperature 40.0 °c

6506 psi

@strain 0.200 %, temperature 104 °f

dam; iso 11403-1 -2
46.01 mpa

@strain 0.210 %, temperature 0.000 °c

6673 psi

@strain 0.210 %, temperature 32.0 °f

dam; iso 11403-1 -2
47.63 mpa

@strain 0.230 %, temperature 0.000 °c

6908 psi

@strain 0.230 %, temperature 32.0 °f

50%rh; iso 11403-1 -2
52.16 mpa

@strain 0.220 %, temperature 23.0 °c

7565 psi

@strain 0.220 %, temperature 73.4 °f

dam; iso 11403-1 -2
52.67 mpa

@strain 0.210 %, temperature -20.0 °c

7639 psi

@strain 0.210 %, temperature -4.00 °f

50%rh; iso 11403-1 -2
53.08 mpa

@strain 1.99 %, temperature 150 °c

7699 psi

@strain 1.99 %, temperature 302 °f

dam; iso 11403-1 -2
54.46 mpa

@strain 0.260 %, temperature 23.0 °c

7899 psi

@strain 0.260 %, temperature 73.4 °f

50%rh; iso 11403-1 -2
55.7 mpa

@strain 5.04 %, temperature 180 °c

8080 psi

@strain 5.04 %, temperature 356 °f

dam; iso 11403-1 -2
56.01 mpa

@strain 4.77 %, temperature 150 °c

8124 psi

@strain 4.77 %, temperature 302 °f

50%rh; iso 11403-1 -2
56.33 mpa

@strain 0.630 %, temperature 90.0 °c

8170 psi

@strain 0.630 %, temperature 194 °f

dam; iso 11403-1 -2
56.48 mpa

@strain 0.200 %, temperature -20.0 °c

8192 psi

@strain 0.200 %, temperature -4.00 °f

dam; iso 11403-1 -2
56.96 mpa

@strain 0.250 %, temperature 40.0 °c

8261 psi

@strain 0.250 %, temperature 104 °f

dam; iso 11403-1 -2
58.58 mpa

@strain 7.15 %, temperature 180 °c

8496 psi

@strain 7.15 %, temperature 356 °f

dam; iso 11403-1 -2
59.14 mpa

@strain 6.74 %, temperature 150 °c

8578 psi

@strain 6.74 %, temperature 302 °f

50%rh; iso 11403-1 -2
60.57 mpa

@strain 1.49 %, temperature 90.0 °c

8785 psi

@strain 1.49 %, temperature 194 °f

50%rh; iso 11403-1 -2
63.55 mpa

@strain 0.280 %, temperature 0.000 °c

9217 psi

@strain 0.280 %, temperature 32.0 °f

dam; iso 11403-1 -2
65.21 mpa

@strain 0.250 %, temperature -20.0 °c

9458 psi

@strain 0.250 %, temperature -4.00 °f

50%rh; iso 11403-1 -2
70.92 mpa

@strain 5.53 %, temperature 150 °c

10290 psi

@strain 5.53 %, temperature 302 °f

dam; iso 11403-1 -2
71.95 mpa

@strain 0.260 %, temperature -20.0 °c

10440 psi

@strain 0.260 %, temperature -4.00 °f

dam; iso 11403-1 -2
74.29 mpa

@strain 7.80 %, temperature 150 °c

10770 psi

@strain 7.80 %, temperature 302 °f

dam; iso 11403-1 -2
74.49 mpa

@strain 0.540 %, temperature 40.0 °c

10800 psi

@strain 0.540 %, temperature 104 °f

50%rh; iso 11403-1 -2
82.47 mpa

@strain 0.390 %, temperature 0.000 °c

11960 psi

@strain 0.390 %, temperature 32.0 °f

50%rh; iso 11403-1 -2
84.81 mpa

@strain 1.25 %, temperature 90.0 °c

12300 psi

@strain 1.25 %, temperature 194 °f

dam; iso 11403-1 -2
85.83 mpa

@strain 4.65 %, temperature 90.0 °c

12450 psi

@strain 4.65 %, temperature 194 °f