zytel® 70g20hsl nc010 nylon 66 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.29 g/cc0.0466 lb/in³dam; iso 1183waterabsorption2.1 %

@temperature 23.0 °c

2.1 %

@temperature 73.4 °f

e 50%rh; dam; iso 62, similar to
6.8 %

@temperature 23.0 °c

6.8 %

@temperature 73.4 °f

saturation, immersed; dam; iso 62, similar to线性成型收缩率,flow0.0040cm/cm

@thickness 2.00 mm

0.0040 in/in

@thickness 0.0787 in

dam; iso 294-4线性成型收缩率，横向0.012 cm/cm

@thickness 2.00 mm

0.012 in/in

@thickness 0.0787 in

dam; iso 294-4机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（m 级）858550%rh; iso2039/2
102102dam; iso 2039/2洛氏硬度（r 级）11511550%rh; iso 2039/2
122122dam; iso 2039/2抗张强度(断裂)103 mpa

@temperature 23.0 °c

14900 psi

@temperature 73.4 °f

50%rh; iso 527
159 mpa

@temperature 23.0 °c

23100 psi

@temperature 73.4 °f

dam; iso 527抗张强度17.5 mpa

@strain 0.530 %, temperature 120 °c

2540 psi

@strain 0.530 %, temperature 248 °f

50%rh; iso 527
18.5 mpa

@strain 0.520 %, temperature 90.0 °c

2680 psi

@strain 0.520 %, temperature 194 °f

50%rh; iso 527
20.5 mpa

@strain 0.520 %, temperature 60.0 °c

2970 psi

@strain 0.520 %, temperature 140 °f

50%rh; iso 527
22.2 mpa

@strain 0.630 %, temperature 120 °c

3220 psi

@strain 0.630 %, temperature 248 °f

dam; iso 527
23.0 mpa

@strain 0.480 %, temperature 40.0 °c

3340 psi

@strain 0.480 %, temperature 104 °f

50%rh; iso 527
24.5 mpa

@strain 0.610 %, temperature 90.0 °c

3550 psi

@strain 0.610 %, temperature 194 °f

dam; iso 527
25.9 mpa

@strain 0.440 %, temperature 23.0 °c

3760 psi

@strain 0.440 %, temperature 73.4 °f

50%rh; iso 527
26.2 mpa

@strain 0.460 %, temperature 60.0 °c

3800 psi

@strain 0.460 %, temperature 140 °f

dam; iso 527
27.7 mpa

@strain 0.270 %, temperature -20.0 °c

4020 psi

@strain 0.270 %, temperature -4.00 °f

50%rh; iso 527
28.8 mpa

@strain 0.330 %, temperature 0.000 °c

4180 psi

@strain 0.330 %, temperature 32.0 °f

50%rh; iso 527
30.6 mpa

@strain 1.06 %, temperature 120 °c

4440 psi

@strain 1.06 %, temperature 248 °f

50%rh; iso 527
33.2 mpa

@strain 0.360 %, temperature 40.0 °c

4820 psi

@strain 0.360 %, temperature 104 °f

dam; iso 527
33.4 mpa

@strain 1.04 %, temperature 90.0 °c

4840 psi

@strain 1.04 %, temperature 194 °f

50%rh; iso 527
35.9 mpa

@strain 0.250 %, temperature 23.0 °c

5210 psi

@strain 0.250 %, temperature 73.4 °f

dam; iso 527
37.4 mpa

@strain 1.04 %, temperature 60.0 °c

5420 psi

@strain 1.04 %, temperature 140 °f

50%rh; iso 527
38.3 mpa

@strain 1.26 %, temperature 120 °c

5550 psi

@strain 1.26 %, temperature 248 °f

dam; iso 527
40.4 mpa

@strain 1.59 %, temperature 120 °c

5860 psi

@strain 1.59 %, temperature 248 °f

50%rh; iso 527
41.2 mpa

@strain 0.960 %, temperature 40.0 °c

5980 psi

@strain 0.960 %, temperature 104 °f

50%rh; iso 527
42.0 mpa

@strain 1.22 %, temperature 90.0 °c

6090 psi

@strain 1.22 %, temperature 194 °f

dam; iso 527
45.1 mpa

@strain 1.56 %, temperature 90.0 °c

6540 psi

@strain 1.56 %, temperature 194 °f

50%rh; iso 527
45.4 mpa

@strain 0.920 %, temperature 60.0 °c

6580 psi

@strain 0.920 %, temperature 140 °f

dam; iso 527
46.8 mpa

@strain 0.880 %, temperature 23.0 °c

6790 psi

@strain 0.880 %, temperature 73.4 °f

50%rh; iso 527