沙伯基础PC/ABS C1100HF物性参数

sabic innovative plastics cycoloy® c1100hf pc+abs(europe-africa-middle east) 物性表

物理性能额定值 (公制)额定值 (英制)测试方法密度1.12 g/cc0.0405 lb/in³iso 1183平衡吸湿0.20%0.20 %23°c / 50% rh; iso 62饱和吸水率0.60 %

@temperature 23.0 °c

0.60 %

@temperature 73.4 °f

iso 62线性成型收缩率,flow0.0050 - 0.0070 cm/cm0.0050 - 0.0070 in/inontensile bar; sabic method熔体流动速率6.0 g/10 min

@load 2.16 kg, temperature 260 °c

6.0 g/10 min

@load 4.76 lb, temperature 500 °f

[cm^3/10 min] melt volume rate; iso 1133
20 g/10 min

@load 5.00 kg, temperature 260 °c

20 g/10 min

@load 11.0 lb, temperature 500 °f

[cm^3/10 min] melt volume rate; iso 1133机械性能额定值 (公制)额定值(英制)测试方法洛氏硬度（r 级）117117iso 2039-2硬度，h358/3099.0 mpa14400 psiiso2039-1抗张强度(断裂)45.0 mpa6530 psi5 mm/min; iso 527
45.0 mpa6530 psi50 mm/min; iso 527抗张强度(屈服)55.0 mpa7980 psi5 mm/min;iso 527
55.0 mpa7980 psi50 mm/min; iso 527伸长率 (断裂)>= 50 %>= 50 %50mm/min; iso 527
120 %120 %5 mm/min; iso 527屈服伸长率4.0 %4.0 %50 mm/min; iso 527
5.0 %5.0 %5 mm/min; iso 527拉伸模量2.40 gpa348 ksi1 mm/min; iso527弯曲强度75.0 mpa10900 psi2 mm/min; iso 178弯曲模量2.30 gpa334 ksi2mm/min; iso 178悬壁梁缺口冲击强度25.0 kj/m²

@temperature -30.0 °c

11.9 ft-lb/in²

@temperature -22.0 °f

80*10*3; iso 180/1a
28.0 kj/m²

@temperature -30.0 °c

13.3 ft-lb/in²

@temperature -22.0 °f

80*10*4; iso 180/1a
50.0 kj/m²

@temperature 23.0 °c

23.8 ft-lb/in²

@temperature 73.4 °f

80*10*3; iso 180/1a悬壁梁无缺口冲击强度nb

@temperature 23.0 °c

nb

@temperature 73.4 °f

80*10*4; iso 180/1u
nb

@temperature -30.0 °c

nb

@temperature -22.0 °f

80*10*4; iso 180/1u简支梁缺口冲击强度2.50 j/cm²

@temperature -30.0 °c

v-notch edgew 80*10*3 sp=62mm; iso 179/1ea
3.00 j/cm²

@temperature -30.0 °c

14.3 ft-lb/in²

@temperature -22.0 °f

v-notch edgew 80*10*4 sp=62mm; iso 179/1ea
5.00 j/cm²

@temperature 23.0 °c

v-notch edgew 80*10*3 sp=62mm; iso 179/1ea
5.50 j/cm²

@temperature 23.0 °c

26.2 ft-lb/in²

@temperature 73.4 °f

v-notch edgew 80*10*4 sp=62mm; iso 179/1ea泰伯磨损，毫克/1000次81

@load 1.00 kg

81

@load 2.20 lb

cs-17; sabic method