sabicinnovative plastics xenoy® iqnh2900

pc+pbt

polymer,thermoplastic,polycarbonate (pc),polycarbonate/polybutyleneterephthalate (pbt) blend, unreinforced,polyester, tp,polybutyleneterephthalate (pbt)sabic innovative plastics (ge plastics)产品说明:

import grade. ul94 v-0 performance with non-brominated flameretardant. pcr% is up to 12% by using valox iq* resin.

物理性能额定值 (公制)额定值 (英制)测试方法比重1.20 g/cc1.20 g/ccastm d792线性成型收缩率,flow0.0050 - 0.0070 cm/cm

@thickness 3.20 mm

0.0050 - 0.0070 in/in

@thickness 0.126 in

sabic method熔体流动速率26 g/10 min

@load 5.00 kg, temperature 266 °c

26 g/10 min

@load 11.0 lb, temperature 511 °f

astm d1238机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)42.0 mpa6090 psitype i, 50 mm/min; astm d638抗张强度(屈服)63.0 mpa9140 psitype i, 50 mm/min; astm d638伸长率 (断裂)65 %65 %type i, 50 mm/min; astm d638屈服伸长率4.0 %4.0 %type i, 50 mm/min; astm d638拉伸模量2.48 gpa360 ksi50 mm/min; astm d638弯曲强度89.0 mpa12900 psi1.3 mm/min, 50 mm span; astm d790弯曲模量2.24 gpa325 ksi1.3 mm/min, 50 mm span; astm d790悬壁梁缺口冲击强度5.50 j/cm10.3 ft-lb/inastm d256落锤总能量65.0 j

@temperature 23.0 °c

47.9 ft-lb

@temperature 73.4 °f

astm d3763热性能额定值 (公制)额定值 (英制)测试方法载荷下热变形温度(1.8 mpa)77.0 °c

@thickness 3.20 mm

171 °f

@thickness 0.126 in

unannealed; astm d648维卡软化温度100 °c212 °frate b/50; astm d1525可燃性(ul94)v-1

@thickness 1.10 mm

v-1

@thickness 0.0433 in

ul 94
v-0

@thickness 1.50 mm

v-0

@thickness 0.0591 in

ul 94
5vb

@thickness 2.50 mm

5vb

@thickness 0.0984 in

ul 94