低价工业园PET美国杜邦 FR543阻燃级

pet美国杜邦 fr543玻纤增强43阻燃v-0

物理性能额定值 (公制)额定值 (英制)测试方法比重1.79 g/cc1.79 g/ccastm d792密度1.79g/cc0.0647 lb/in³iso 1183填料含量43 %43 %
water absorption0.060 %

@temperature 23.0 °c

0.060 %

@temperature 73.4 °f

50%rh,23°c,24h; astm d570
0.11 %

@temperature 23.0 °c

0.11 %

@temperature 73.4 °f

e 50%rh; iso 62, similar to
0.62 %

@temperature 23.0 °c

0.62 %

@temperature 73.4 °f

saturation, immersed; iso 62, similar to线性成型收缩率0.0013 cm/cm

@thickness 1.57 mm

0.0013 in/in

@thickness 0.0618 in

flow
0.0020 cm/cm

@thickness 3.20 mm

0.0020 in/in

@thickness 0.126 in

flow
0.0048 cm/cm

@thickness 1.57 mm

0.0048 in/in

@thickness 0.0618 in

transverse
0.0065 cm/cm

@thickness 3.20 mm

0.0065 in/in

@thickness 0.126 in

transverse线性成型收缩率,flow0.0025 cm/cm0.0025 in/inannealed; iso294-4
0.0020 cm/cm

@thickness 2.00 mm

0.0020 in/in

@thickness 0.0787 in

iso 294-4线性成型收缩率，横向0.0105 cm/cm0.0105 in/inannealed; iso 294-4
0.0075 cm/cm

@thickness 2.00 mm

0.0075 in/in

@thickness 0.0787 in

iso 294-4化合物熔体指数6.0 g/10 min

@load 2.16 kg, temperature 280 °c

6.0 g/10 min

@load 4.76 lb, temperature 536 °f

cm3/10 min; iso 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（m 级）9595astmd785
102102iso 2039/2洛氏硬度（r 级）120120astm d785
122122iso 2039/2抗张强度(断裂)170 mpa

@temperature 23.0 °c

24700 psi

@temperature 73.4 °f

iso 527抗张强度55.2 mpa

@temperature 150 °c

8010 psi

@temperature 302 °f

astm d638
86.5 mpa

@temperature 90.0 °c

12500 psi

@temperature 194 °f

astm d638
172 mpa

@temperature 23.0 °c

24900 psi

@temperature 73.4 °f

astm d638
210 mpa

@temperature -40.0 °c

30500 psi

@temperature -40.0 °f

astm d638
22.4 mpa

@strain 0.470 %, temperature 150 °c

3250 psi

@strain 0.470 %, temperature 302 °f

iso 527
27.22 mpa

@strain 0.430 %, temperature 120 °c

3948 psi

@strain 0.430 %, temperature 248 °f

iso 527
27.5 mpa

@strain 0.160 %, temperature 0.000 °c

3990 psi

@strain 0.160 %, temperature 32.0 °f

iso 527
28.39 mpa

@strain 0.350 %, temperature 90.0 °c

4118 psi

@strain 0.350 %, temperature 194 °f

iso 527
29.0 mpa

@strain 0.140 %, temperature -40.0 °c

4210 psi

@strain 0.140 %, temperature -40.0 °f

iso 527
30.0 mpa

@strain 0.210 %, temperature 40.0 °c

4350 psi

@strain 0.210 %, temperature 104 °f

iso 527
31.0 mpa

@strain 0.180 %, temperature 23.0 °c

4500 psi

@strain 0.180 %, temperature 73.4 °f

iso 527
34.9 mpa

@strain 0.940 %, temperature 150 °c

5060 psi

@strain 0.940 %, temperature 302 °f

iso 527
35.57 mpa

@strain 0.310 %, temperature 60.0 °c

5159 psi

@strain 0.310 %, temperature 140 °f

iso 527
41.5 mpa

@strain 1.41 %, temperature 150 °c

6020 psi

@strain 1.41 %, temperature 302 °f

iso 527
41.8 mpa

@strain 0.830 %, temperature 120 °c

6060 psi

@strain 0.830 %, temperature 248 °f

iso 527
45.7 mpa

@strain 1.87 %, temperature 150 °c

6630 psi

@strain 1.87 %, temperature 302 °f

iso 527
47.19 mpa

@strain 0.690 %, temperature 90.0 °c

6844 psi

@strain 0.690 %, temperature 194 °f

iso 527
49.1 mpa

@strain 2.34 %, temperature 150 °c

7120 psi

@strain 2.34 %, temperature 302 °f

iso 527
50.35 mpa

@strain 0.370 %, temperature 40.0 °c

7303 psi

@strain 0.370 %, temperature 104 °f

iso 527
50.8 mpa

@strain 1.23 %, temperature 120 °c

7370 psi

@strain 1.23 %, temperature 248 °f

iso 527
51.7 mpa

@strain 2.81 %, temperature 150 °c

7500 psi

@strain 2.81 %, temperature 302 °f

iso 527
52.4 mpa

@strain 0.320 %, temperature 0.000 °c

7600 psi

@strain 0.320 %, temperature 32.0 °f

iso 527
53.8 mpa

@strain 3.28 %, temperature 150 °c

7800 psi

@strain 3.28 %, temperature 302 °f

iso 527
53.9 mpa

@strain 0.280 %, temperature -40.0 °c

7820 psi

@strain 0.280 %, temperature -40.0 °f

iso 527
55.0 mpa

@strain 0.520 %, temperature 60.0 °c

7980 psi

@strain 0.520 %, temperature 140 °f

iso 527
55.6 mpa

@strain 3.75 %, temperature 150 °c

8060 psi

@strain 3.75 %, temperature 302 °f

iso 527
56.4 mpa

@strain 0.350 %, temperature 23.0 °c

8180 psi

@strain 0.350 %, temperature 73.4 °f

iso 527
56.85 mpa

@strain 1.63 %, temperature 120 °c

8245 psi

@strain 1.63 %, temperature 248 °f

iso 527
57.1 mpa

@strain 4.21 %, temperature 150 °c

8280 psi

@strain 4.21 %, temperature 302 °f

iso 527
58.5 mpa

@strain 4.69 %, temperature 150 °c

8480 psi

@strain 4.69 %, temperature 302 °f

iso 527
59.61 mpa

@strain 1.03 %, temperature 90.0 °c

8646 psi

@strain 1.03 %, temperature 194 °f

iso 527
61.26 mpa

@strain 2.04 %, temperature 120 °c

8885 psi

@strain 2.04 %, temperature 248 °f

iso 527
64.62 mpa

@strain 2.44 %, temperature 120 °c

9372 psi

@strain 2.44 %, temperature 248 °f

iso 527
67.28 mpa

@strain 2.84 %, temperature 120 °c

9758 psi

@strain 2.84 %, temperature 248 °f

iso 527
68.2 mpa

@strain 1.37 %, temperature 90.0 °c

9890 psi

@strain 1.37 %, temperature 194 °f

iso 527
69.36 mpa

@strain 3.24 %, temperature 120 °c

10060 psi

@strain 3.24 %, temperature 248 °f

iso 527
71.09 mpa

@strain 3.65 %, temperature 120 °c

10310 psi

@strain 3.65 %, temperature 248 °f

iso 527
71.87 mpa

@strain 0.730 %, temperature 60.0 °c

10420 psi

@strain 0.730 %, temperature 140 °f

iso 527
72.35 mpa

@strain 4.05 %, temperature 120 °c

10490 psi

@strain 4.05 %, temperature 248 °f

iso 527
72.8 mpa

@strain 0.560 %, temperature 40.0 °c

10600 psi

@strain 0.560 %, temperature 104 °f

iso 527
74.5 mpa

@strain 0.480 %, temperature 23.0 °c

10800 psi

@strain 0.480 %, temperature 73.4 °f

iso 527
74.52 mpa

@strain 1.70 %, temperature 90.0 °c

10810 psi

@strain 1.70 %, temperature 194 °f

iso 527
75.5 mpa

@strain 0.420 %, temperature -40.0 °c

11000 psi

@strain 0.420 %, temperature -40.0 °f

iso 527
75.9 mpa

@strain 0.470 %, temperature 0.000 °c

11000 psi

@strain 0.470 %, temperature 32.0 °f

iso 527
79.34 mpa

@strain 2.04 %, temperature 90.0 °c

11510 psi

@strain 2.04 %, temperature 194 °f

iso 527
83.14 mpa

@strain 2.41 %, temperature 90.0 °c

12060 psi

@strain 2.41 %, temperature 194 °f

iso 527
83.19 mpa

@strain 0.940 %, temperature 60.0 °c

12070 psi

@strain 0.940 %, temperature 140 °f

iso 527
85.76 mpa

@strain 2.75 %, temperature 90.0 °c

12440 psi

@strain 2.75 %, temperature 194 °f

iso 527