PC沙伯基础943A

sabic沙伯基础创新lexan pc 943a物性表

以下是sabic沙伯基础创新lexan pc 943a中英文物性表资料

sabic innovative plastics lexan® 943a pc

特性：中等粘度，阻燃v0(3.0mm)。紫外线稳定。优良外观，透明

material notes:

lexan 943a is a medium viscosity flame retardant,uv-stabilized grade. ul-94 v0 listed and available in transparentand tints..

physical properties物理性质

metric公制数据

english英制数据

comments测试方法

density密度 

1.20 g/cc

0.0434 lb/in³

iso 1183

moisture absorption ate吸湿平衡 

0.15 %

0.15 %

23°c / 50% rh; iso 62

water absorption吸水率 atsaturation 

0.35 %
@temperature 23.0°c

0.35 %
@temperature 73.4°f

iso 62

linear mold shrinkage,flow线性收缩率/流动 

0.0050 - 0.0070 cm/cm

0.0050 - 0.0070 in/in

on tensile bar; sabic method

melt flow熔体流动速率 

9.0 g/10min
@load 1.20kg,
temperature 300 °c

9.0 g/10min
@load 2.65lb,
temperature 572 °f

[cm^3/10 min] melt volume rate; iso 1133

mechanical properties力学性能

metric公制数据

english英制数据

comments测试方法

hardness, h358/30 

95.0 mpa

13800 psi

iso 2039-1

tensile strength atbreak断裂拉伸强度 

65.0 mpa

9430 psi

50 mm/min; iso 527

tensile strength,yield屈服拉伸强度 

63.0 mpa

9140 psi

50 mm/min; iso 527

elongation at break断裂伸长率 

100 %

100 %

50 mm/min; iso 527

elongation at yield屈服伸长率 

6.0 %

6.0 %

50 mm/min; iso 527

tensile modulus拉伸模量 

2.35 gpa

341 ksi

1 mm/min; iso 527

flexural yieldstrength弯曲屈服强度 

90.0 mpa

13100 psi

2 mm/min; iso 178

flexural modulus弯曲弹性模量 

2.30 gpa

334 ksi

2 mm/min; iso 178

izod impact,notched悬臂梁缺口冲击强度 (iso) 

12.0 kj/m²
@temperature-30.0 °c

5.71 ft-lb/in²
@temperature-22.0 °f

80*10*3; iso 180/1a

70.0 kj/m²
@temperature23.0 °c

33.3 ft-lb/in²
@temperature73.4 °f

80*10*3; iso 180/1a

izod impact,unnotched悬臂梁无缺口冲击强度 (iso)  

nb
@temperature 23.0°c

nb
@temperature 73.4°f

80*10*3; iso 180/1u

nb
@temperature -30.0°c

nb
@temperature -22.0°f

80*10*3; iso 180/1u

charpy impactunnotched夏比缺口试样冲击 

nb
@temperature 23.0°c

nb
@temperature 73.4°f

edgew 80*10*3 sp=62mm; iso 179/1eu

nb
@temperature -30.0°c

nb
@temperature -22.0°f

edgew 80*10*3 sp=62mm; iso 179/1eu

charpy impact, notched夏比缺口冲击 

1.40 j/cm²
@temperature-30.0 °c

6.66 ft-lb/in²
@temperature-22.0 °f

v-notch edgew 80*10*3 sp=62mm; iso 179/1ea

3.00 j/cm²
@temperature23.0 °c

14.3 ft-lb/in²
@temperature73.4 °f

iso 179/2c

7.30 j/cm²
@temperature23.0 °c

34.7 ft-lb/in²
@temperature73.4 °f

v-notch edgew 80*10*3 sp=62mm; iso 179/1ea

taber abrasion, mg/1000cycles周期泰伯磨耗 

10
@load 1.00 kg

10
@load 2.20 lb

cs-17; sabic method

electrical properties电性能

metric公制数据

english英制数据

comments测试方法

volume resistivity体积电阻率 

>= 1.00e+15 ohm-cm

>= 1.00e+15 ohm-cm

iec 60093

surface resistance表面电阻 

>= 1.00e+15 ohm

>= 1.00e+15 ohm

roa; iec 60093

dielectric constant介电常数 

2.7
@frequency 1.00e+6hz

2.7
@frequency 1.00e+6hz

iec 60250

2.7
@frequency 50.0 - 60.0hz

2.7
@frequency 50.0 - 60.0hz

iec 60250

dielectric strength介电强度 

17.0 kv/mm
@thickness3.20 mm

432 kv/in
@thickness0.126 in

in oil; iec 60243-1

dissipation factor耗散因数 

0.0010
@frequency 50.0 - 60.0hz

0.0010
@frequency 50.0 - 60.0hz

iec 60250

0.010
@frequency 1.00e+6hz

0.010
@frequency 1.00e+6hz

iec 60250

comparative trackingindex跟踪指数 

225 v

225 v

iec 60112

thermal properties热性能

metric公制数据

english英制数据

comments测试方法

cte, linear, parallel toflow线性热膨胀系数 

70.0 µm/m-°c
@temperature23.0 - 80.0 °c

38.9 µin/in-°f
@temperature73.4 - 176 °f

iso 11359-2

thermal conductivity导热系数 

0.200 w/m-k

1.39 btu-in/hr-ft²-°f

iso 8302

hot ball pressure test热球压力测试 

<= 140 °c

<= 284 °f

iec 60695-10-2

deflection temperatureat热变形温度  0.46 mpa (66psi) 

136 °c

277 °f

edgew 120*10*4 sp=100mm; iso 75/be

deflection temperatureat热变形温度  1.8 mpa (264psi) 

125 °c

257 °f

edgew 120*10*4 sp=100mm; iso 75/ae

vicat softening point维卡软化点

141 °c

286 °f

rate b/50; iso 306

142 °c

288 °f

rate b/120; iso 306

ul rti, electrical相对温度指数 

130 °c

266 °f

ul 746b

ul rti, mechanical withimpact机械冲击热指数 

120 °c

248 °f

ul 746b

ul rti, mechanical withoutimpact无机械冲击热指数 

125 °c

257 °f

ul 746b

flammability, ul94阻燃等级 

v-2
@thickness 1.50mm

v-2
@thickness 0.0591in

ul 94

v-0
@thickness 3.00mm

v-0
@thickness 0.118in

ul 94

flammability test 

1.5

1.5

[mm], needle flame test, 10 s , passes at; iec60695-2-2

oxygen index氧指数 

35 %

35 %

loi; iso 4589

glow wire test灼热丝测试 

850 °c
@thickness1.00 mm

1560 °f
@thickness0.0394 in

glow wire flammability index; iec 60695-2-12

960 °c
@thickness1.60 mm

1760 °f
@thickness0.0630 in

glow wire flammability index; iec 60695-2-12

optical properties光学性质

metric公制数据

english英制数据

comments测试方法

refractive index折射率 

1.586

1.586

iso 489

transmission, visible透光率 

88 %
@thickness 2.54mm

88 %
@thickness 0.100in

astm d 1003