abs台湾台化ag10np详情
性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)
astm d638/iso 527490(48)kg/cm²(mpa)[lb/in2]断裂伸长率
astm d638/iso 527
%拉伸模量
astm d638/iso 527
kg/cm²(mpa)[lb/in2]拉伸屈服伸长率(延伸率)
astm d638/iso 527
%拉伸断裂伸长率(延伸率)
astm d638/iso 527
%弯曲模量(弯曲弹性率)
astm d790/iso 17825000(2450)kg/cm²(mpa)[lb/in2]弯曲强度
astm d790/iso 178740(73)kg/cm²(mpa)[lb/in2]洛氏硬度
astm d785r-102
izod 缺口冲击强度1/4" 23℃astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in1/4" -30℃astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in1/8" 23℃astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in1/8" -30℃astm d256/iso 179
kg·cm/cm(j/m)ft·lb/incharpy冲击强度23℃ （缺口）astm d256/iso17946(451)kg·cm/cm(j/m)ft·lb/in-30℃（缺口）astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in23℃（无缺口）astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in-30℃（无缺口）astm d256/iso 179
kg·cm/cm(j/m)ft·lb/in物性性能比重（密度）
astm d792/iso 11831.04
成型收缩率
astm d9550.4~0.7%熔融指数（流动系数）200℃/5kgastm d1238/iso11336.5g/10min220℃/10kgastm d1238/iso 1133
g/10min吸水率 23℃/24h
astm d570/iso 62
%热性能热变形温度退火astm d648/iso 75104℃（℉）未退火astm d648/iso7592℃（℉）维卡软化点
astm d1525/iso r306107℃（℉）熔点
-
℃（℉）燃烧性（率）
ul941/16
线性膨胀系数
astm d696/iso 11359
mm/mm.℃加工条件干燥条件
加工温度射嘴
℃料筒前段
℃料筒中段
℃料筒后段
℃熔体温度
℃模具温度
℃压力注塑压力
mpa保压压力
mpa背压
mpa螺杆转速
rpm其他备注
颜色
特性押出成型用、超高耐冲击性、高刚性用途押出成型制品、安全帽、管状制品
ABS台湾台化AG10NP