供应基础创新塑料c1200hf高耐热pcabs,低温延展性,高流动性,良好的可加工性,良好的外观,优异的流动性、抗冲击性、耐高温性。低温延性。适合于汽车、器具和电气元件。
基础创新c1200hf物性:
physical | nominal value | unit | test method |
density / specific gravity | 1.15 | g/cm³ | astm d792 |
melt mass-flow rate (mfr) (260°c/5.0kg) | 19 | g/10 min | astm d1238 |
molding shrinkage - flow (3.20mm) | 0.50 to 0.70 | % | internal method |
mechanical | nominal value | unit | test method |
tensile modulus 2 | 2280 | mpa | astm d638 |
tensilestrength 3 (yield) | 57.2 | mpa | astm d638 |
tensileelongation 3 (yield) | 5.0 | % | astm d638 |
tensileelongation 3 (break) | 100 | % | astm d638 |
flexuralmodulus 4 (50.0 mmspan) | 2340 | mpa | astm d790 |
flexuralstrength 4 (yield, 50.0 mmspan) | 88.3 | mpa | astm d790 |
impact | nominal value | unit | test method |
notched izod impact | astm d256 | ||
-30°c | 480 | j/m | |
23°c | 590 | j/m | |
instrumented dart impact | astm d3763 | ||
-30°c, total energy | 54.2 | j | |
23°c, total energy | 54.2 | j | |
thermal | nominal value | unit | test method |
deflection temperature under load (0.45mpa, unannealed, 3.20 mm) | 129 | °c | astm d648 |
deflection temperature under load (1.8mpa, unannealed, 3.20 mm) | 113 | °c | astm d648 |
vicat softening temperature | 130 | °c | iso 306/b50 |
clte - flow (-40 to 40°c) | 7.2e-5 | cm/cm/°c | astm e831 |
rti elec | 105 | °c | ul 746 |
rti imp | 80.0 | °c | ul 746 |
rti str | 105 | °c | ul 746 |
electrical | nominal value | unit | test method |
comparative tracking index (cti) | plc 2 | ul 746 | |
high amp arc ignition (hai) | plc 1 | ul 746 | |
hot-wire ignition (hwi) | plc 3 | ul 746 | |
flammability | nominal value | unit | test method |
flame rating (1.2 mm) | hb | ul 94 |