| 熔体质量流动速率 | ISO1133 | 14 | g/10min | |
| 熔体体积流动速率 | 190°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| 收缩率 | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 1.9 | % | |
| 吸水率 | 饱和,23°C,2.00mm | ISO62 | 0.90 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.30 | % | |
| 拉伸模量 | ISO527-2 | 3400 | Mpa | |
| 拉伸强度 | 屈服 | ISO527-2 | 74.0 | Mpa |
| 伸长率 | 屈服 | ISO527-2 | 12 | % |
| 标称拉伸断裂应变 | ISO527-2 | 20 | % | |
| 弯曲模量 | ISO178 | 3200 | Mpa | |
| 弯曲强度 | 3.5%应变 | ISO178 | 85.0 | Mpa |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 160 | kJ/m² |
| 23°C | ISO179/1eU | 160 | kJ/m² | |
| -30°C | ISO179/1eA | 6.0 | kJ/m² | |
| 23°C | ISO179/1eA | 7.0 | kJ/m² | |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 163 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 105 | °C | |
| 熔融温度 | ISO11357-3 | 178 | °C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| 燃烧速率 | 1.00mm | ISO3795 | <100 | mm/min |
| UL阻燃等级 | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS可燃性 | FMVSS302 | B | ||
| 雾化 | F-value(refraction) | ISO6452 | 97 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g | |
| Emission | VDA275 | <8.00 | mg/kg |
美国杜邦PA66,美国杜邦POM,沙伯基础PC,德国巴斯夫 TPU, 基础创新 PPO,日本宝理 LCP,日本宝理 PPS,基础创新塑料 PBT,基础创新塑料 PEI,美国杜邦 TPEE
研发、生产、加工、销售：塑料制品。(依法须经批准的项目，经相关部门批准后方可开展经营活动)〓
东莞市豪业塑料有限公司是以生产改性工程塑料(PC透明、瓷白、遮光瓷白、半透、黑色：PC光扩散料、PC/ABS本色、黑色、灰色：ABS本色、黑色等阻燃、非阻燃环保系列）为主的企业。自2002年建厂以来，以“质量为本.顾客至上.信誉第一”为企业的经营宗旨。多年来承蒙新老客户的信赖与支持，规模日益壮大。通过多年与国内外知名生产厂家及贸易商伙伴合作，以及其具有竞争力的价格优势和专业高效的服务体系，已成为珠江三角洲知名的塑料原料改性生产企业。我厂...