供应沙伯基础创新457玻纤增强阻燃PBT，防火5VA，韧性好

供应沙伯基础创新457玻纤增强阻燃PBT，防火5VA，韧性好，原厂原包，随货提供ROHS报告，UL认证，FDA认证，出厂材质证明（COA）及物质安全资料表(SDS)。 

沙伯基础创新PBT 457物性表：

MECHANICALTensile Stress, brk, Type I, 5 mm/min (ASTM D638)Flexural Stress, break, 2 mm/min (ISO 178)Tensile Stress, yield, 5 mm/min (ISO 527)Tensile Strain, yld, Type I, 5 mm/min (ASTM D638)Flexural Modulus, 2 mm/min (ISO 178)Tensile Strain, brk, Type I, 5 mm/min (ASTM D638)Tensile Strain, break, 5 mm/min (ISO 527)Tensile Strain, yield, 5 mm/min (ISO 527)Tensile Stress, yld, Type I, 5 mm/min (ASTM D638)Tensile Stress, break, 5 mm/min (ISO 527)Tensile Modulus, 5 mm/min (ASTM D638)Flexural Stress, yield, 2 mm/min (ISO 178)Tensile Modulus, 1 mm/min (ISO 527)Flexural Strain, break, 2 mm/min (ISO 178)Ball Indentation Hardness, H358/30 (ISO 2039-1)Hardness, Rockwell R (ISO 2039-2)IMPACTIzod Impact, unnotched 80*10*4 -30°C (ISO 180/1U)Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm (ISO 179/1eA)Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm (ISO 179/1eA)Izod Impact, unnotched, -30°C (ASTM D4812)Izod Impact, notched 80*10*4 +23°C (ISO 180/1A)Izod Impact, notched, 0°C (ASTM D256)Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm (ISO 179/1eU)Charpy Impact, notched, 23°C (ISO 179/2C)Izod Impact, unnotched, 23°C (ASTM D4812)Charpy Impact, unnotched, -30°C (ISO 179/2C)Charpy Impact, notched, -30°C (ISO 179/2C)Izod Impact, notched 80*10*4 0°C (ISO 180/1A)Izod Impact, notched, 23°C (ASTM D256)Izod Impact, unnotched 80*10*4 +23°C (ISO 180/1U)Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm (ISO 179/1eU)Izod Impact, notched 80*10*4 -30°C (ISO 180/1A)Izod Impact, notched, -30°C (ASTM D256)Charpy Impact, unnotched, 23°C (ISO 179/2C)THERMALHDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm (ISO 75/Be)CTE, 23°C to 150°C, xflow (ISO 11359-2)CTE, -40°C to 40°C, flow (ISO 11359-2)Relative Temp Index, Mech w/o impact (UL 746B)Vicat Softening Temp, Rate A/50 (ASTM D1525)CTE, -40°C to 40°C, xflow (ISO 11359-2)CTE, 23°C to 80°C, flow (ISO 11359-2)Vicat Softening Temp, Rate B/120 (ISO 306)Relative Temp Index, Mech w/impact (UL 746B)CTE, 23°C to 150°C, flow (ISO 11359-2)Relative Temp Index, Elec (UL 746B)HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm (ISO 75/Af)HDT, 0.45 MPa, 3.2 mm, unannealed (ASTM D648)Vicat Softening Temp, Rate A/50 (ISO 306)HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm (ISO 75/Bf)Vicat Softening Temp, Rate B/50 (ASTM D1525)HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm (ISO 75/Ae)Vicat Softening Temp, Rate B/50 (ISO 306)CTE, 23°C to 80°C, xflow (ISO 11359-2)HDT, 1.82 MPa, 3.2mm, unannealed (ASTM D648)Ball Pressure Test, 125°C +/- 2°C (IEC 60695-10-2)PHYSICALWater Absorption, (23°C/saturated) (ISO 62-1)Melt Viscosity, 260°C, 1500 sec-1 (ISO 11443)Melt Volume Rate, MVR at 265°C/5.0 kg (ISO 1133)Melt Volume Rate, MVR at 250°C/2.16 kg (ISO 1133)Melt Volume Rate, MVR at 250°C/5.0 kg (ISO 1133)Moisture Absorption (23°C / 50% RH) (ISO 62)Specific Gravity (ASTM D792)Mold Shrinkage on Tensile Bar, xflow (SABIC method)Density (ISO 1183)Mold Shrinkage on Tensile Bar, flow (SABIC method)Filler Content (ASTM D229)Melt Flow Rate, 266°C/5.0 kgf (ASTM D1238)ELECTRICALSurface Resistivity, ROA (IEC 60093)Dielectric Strength, in oil, 0.8 mm (IEC 60243-1)High Voltage Arc Resistance {PLC) (UL 746A)Dissipation Factor, 1 MHz (ASTM D150)Dissipation Factor, 1 MHz (IEC 60250)Hot Wire Ignition {PLC) (UL 746A)High Voltage Arc Track Rate {PLC} (UL 746A)Comparative Tracking Index (UL) {PLC} (UL 746A)Volume Resistivity (ASTM D257)Dielectric Strength, in oil, 3.2 mm (ASTM D149)Relative Permittivity, 1 MHz (ASTM D150)Dissipation Factor, 100 Hz (IEC 60250)Dielectric Strength, in oil, 1.6 mm (ASTM D149)Comparative Tracking Index (IEC 60112)High Ampere Arc Ign, surface {PLC} (UL 746A)Dielectric Strength, in oil, 1.6 mm (IEC 60243-1)Volume Resistivity (IEC 60093)Relative Permittivity, 1 MHz (IEC 60250)Relative Permittivity, 50/60 Hz (IEC 60250)Dissipation Factor, 50/60 Hz (IEC 60250)Dielectric Strength, in oil, 3.2 mm (IEC 60243-1)Relative Permittivity, 100 Hz (IEC 60250)FLAME CHARACTERISTICSGlow Wire Flammability Index 960°C, passes at (IEC60695-2-12)Oxygen Index (LOI) (ISO 4589)UL Recognized, 94V-0 Flame Class Rating (UL 94)UL Recognized, 94-5VA Flame Class Rating (UL 94)

79 MPa
120 MPa
75 MPa
3 %
3700 MPa
3 %
3 %
3 %
79 MPa
75 MPa
4100 MPa
120 MPa
4200 MPa
4 %
180 MPa
120 -
25 kJ/m²
7 kJ/m²
6 kJ/m²
320 J/m
3 kJ/m²
32 J/m
30 kJ/m²
4 kJ/m²
275 J/m
30 kJ/m²
3 kJ/m²
3 kJ/m²
32 J/m
25 kJ/m²
30 kJ/m²
3 kJ/m²
32 J/m
30 kJ/m²
200 °C
1.34E-04 1/°C
5.72E-05 1/°C
140 °C
220 °C
8.82E-05 1/°C
8.E-05 1/°C
210 °C
120 °C
6.61E-05 1/°C
120 °C
145 °C
200 °C
220 °C
200 °C
188 °C
140 °C
190 °C
1.E-04 1/°C
145 °C
PASSES -
0.28 %
190 Pa-s
55 cm³/10 min
11 cm³/10 min
30 cm³/10 min
0.06 %
1.44 -
0.9-1.2 %
1.45 g/cm³
0.8-1 %
7 %
65 g/10 min
>1.E+15 Ω
29 kV/mm
7 PLC Code
0.02 -
0.02 -
3 PLC Code
4 PLC Code
3 PLC Code
>5.5E+16 Ω.cm
15 kV/mm
3.4 -
0.002 -
23 kV/mm
175 V
3 PLC Code
23 kV/mm
>1.E+15 Ω.cm
3.4 -
3 -
0.002 -
15 kV/mm
3.5 -
1 mm
30 %
0.71 mm
3 mm