Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
This data was supplied by SABIC-IP for the Americas region.
物性信息：
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| 密度 | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| 平衡吸湿 | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| 饱和吸水率 | 0.35 % @Temperature 23.0 °C | 0.35 % @Temperature 73.4 °F | ISO 62 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 16 g/10 min @Load 1.20 kg, Temperature 300 °C | 16 g/10 min @Load 2.65 lb, Temperature 572 °F | [cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 17.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 17.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D 1238 |
| 抗张强度(断裂) | 67.0 MPa | 9720 psi | Type I, 50 mm/min; ASTM D 638 |
| 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 | |
| 抗张强度(屈服) | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
| 67.0 MPa | 9720 psi | 50 mm/min; ISO 527 | |
| 伸长率 (断裂) | >= 100 % | >= 100 % | Type I, 50 mm/min; ASTM D 638 |
| >= 100 % | >= 100 % | 50 mm/min; ISO 527 | |
| 屈服伸长率 | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 |
| 2.40 GPa | 348 ksi | 5 mm/min; ASTM D 638 | |
| 弯曲强度 | 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 | |
| 弯曲模量 | 2.45 GPa | 355 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.45 GPa | 355 ksi | 2 mm/min; ISO 178 | |
| 悬壁梁缺口冲击强度 | 1.30 J/cm @Temperature -30.0 °C | 2.44 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 7.80 J/cm @Temperature 23.0 °C | 14.6 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | 80*10*3; ISO 180/1A | |
| 25.0 kJ/m² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 80*10*3; ISO 180/1A | |
| 悬壁梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 80*10*3; ISO 180/1U |
| 简支梁无缺口冲击强度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 简支梁缺口冲击强度 | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 3.00 J/cm² @Temperature 23.0 °C | 14.3 ft-lb/in² @Temperature 73.4 °F | V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| 冲击试验 | 80.0 J @Temperature 23.0 °C | 59.0 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| 线形热膨胀系数 - 流动 | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| 线性热膨胀系数,横向流动 | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | 38.9 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 载荷下热变形温度(1.8 MPa) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 133 °C @Thickness 3.20 mm | 271 °F @Thickness 0.126 in | unannealed; ASTM D 648 | ||
| 维卡软化温度 | 136 °C | 277 °F | Rate B/50; ISO 306 | |
| 137 °C | 279 °F | Rate B/120; ISO 306 | ||
| 137 °C | 279 °F | Rate B/50; ASTM D 1525 | ||
| 可燃性(UL94) | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | UL 94 by SABIC-IP | |
| 灼热丝易燃指数 | 825 °C @Thickness 1.00 mm | 1520 °F @Thickness 0.0394 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | |
| 825 °C @Thickness 2.00 mm | 1520 °F @Thickness 0.0787 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | ||
| 825 °C @Thickness 2.50 mm | 1520 °F @Thickness 0.0984 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | ||
| 825 °C @Thickness 3.00 mm | 1520 °F @Thickness 0.118 in | Glow Wire Ignitability Temperature; IEC 60695-2-13 | ||
| 960 °C @Thickness 1.50 mm | 1760 °F @Thickness 0.0591 in | Glow Wire Flammability Index; IEC 60695-2-12 |
| 雾度 | 0.60 % @Thickness 2.54 mm | 0.60 % @Thickness 0.100 in | ASTM D 1003 |
| Transmission, Visible | 89 % @Thickness 2.54 mm | 89 % @Thickness 0.100 in | ASTM D 1003 |
| 球压试验，125°C+/-2℃ | passes | IEC 60695-10-2 |
主营塑胶原料：PC , PPA , POM , PA6 , PA66 , PBT , PET , PC/ABS , PMMA ,TPSIV , GPPS , HIPS , PP , PE , EVA , EAA , PPO , PA11, PA12 , TPU , TPV , TPEE, POE , PPS , LCP
一般项目：合成材料销售；合成纤维销售；工程塑料及合成树脂销售；塑料制品销售；生物基材料销售；高性能纤维及复合材料销售；玻璃纤维增强塑料制品销售。（除依法须经批准的项目外，凭营业执照依法自主开展经营活动）
本公司长期经营各种塑胶原料. 长期经营的品牌有杜邦,旭化成,GE,三菱,巴斯夫,LG,东丽,LNP,南亚,帝人,拜耳,台湾长春，台湾奇美，台湾台化等 通用塑料：ABS、AS、GPPS、HIPS、PP、PE、食品级ABS、AS、PS、PP等。工程塑料：COC镜头料、PMMA、POM、PC、PC/ABS、PA66、PA6、PPE、PBT、PET、ASA、PPO、PC PBT、PBT/PC 、CA；PA46、PA9T、PA6T、PA12、PA...