PC 沙伯基础(Sabic) ML6018R 缺口 Izod 11.0;较高流动性和 抗冲击性
- 报价
- 请来电询价
- 联系手机
- 15118275316
- 微信号
- 15118275316
- 品牌
- PC 沙伯基础(Sabic)
- 型号
- ML6018R
- 特性
- 抗冲击性
Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明：
ML6018R is a low viscosity grade exhibiting a high impact performance over standard PC. It contains an enhanced release-agent. Opaque colours only.
This data was supplied by SABIC-IP for the Asia Pacific region.
物性信息：
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D 792 |
| 抗张强度(断裂) | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
| 抗张强度(屈服) | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
| 伸长率 (断裂) | 103 % | 103 % | Type I, 50 mm/min; ASTM D 638 |
| 拉伸模量 | 1.58 GPa | 229 ksi | 50 mm/min; ASTM D 638 |
| 弯曲强度 | 75.0 MPa | 10900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 弯曲模量 | 1.83 GPa | 265 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | 4.80 J/cm @Temperature -30.0 °C | 8.99 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 5.66 J/cm @Temperature 23.0 °C | 10.6 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| 冲击试验 | 70.0 J @Temperature 23.0 °C | 51.6 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| 载荷下热变形温度(1.8 MPa) | 115 °C @Thickness 6.40 mm | 239 °F @Thickness 0.252 in | unannealed; ASTM D 648 |
东莞市晨希塑胶原料有限公司
主营塑胶原料：PC , PPA , POM , PA6 , PA66 , PBT , PET , PC/ABS , PMMA ,TPSIV , GPPS , HIPS , PP , PE , EVA , EAA , PPO , PA11, PA12 , TPU , TPV , TPEE, POE , PPS , LCP
一般项目：合成材料销售；合成纤维销售；工程塑料及合成树脂销售；塑料制品销售；生物基材料销售；高性能纤维及复合材料销售；玻璃纤维增强塑料制品销售。（除依法须经批准的项目外，凭营业执照依法自主开展经营活动）
本公司长期经营各种塑胶原料. 长期经营的品牌有杜邦,旭化成,GE,三菱,巴斯夫,LG,东丽,LNP,南亚,帝人,拜耳,台湾长春，台湾奇美，台湾台化等 通用塑料：ABS、AS、GPPS、HIPS、PP、PE、食品级ABS、AS、PS、PP等。工程塑料：COC镜头料、PMMA、POM、PC、PC/ABS、PA66、PA6、PPE、PBT、PET、ASA、PPO、PC PBT、PBT/PC 、CA；PA46、PA9T、PA6T、PA12、PA...