供应赢创德固赛E47-S1聚酰胺PA12弹性体高韧性柔软尼龙12消音齿轮用

供应赢创德固赛E47-S1聚酰胺PA12弹性体高韧性柔软尼龙12消音齿轮用，原厂原包，随货提供ROHS报告，UL认证，FDA认证，出厂材质证明（COA）及物质安全资料表(SDS)。

赢创德固赛PA12 E47-S1物性表：

Physical

Nominal Value

Unit

Test Method

Density / Specific Gravity

1.02

g/cm³

ASTM D792

Density

1.02

g/cm³

ISO 1183

Melt Volume-Flow Rate (MVR) (240°C/2.16 kg)

28

cm³/10min

ISO 1133

Molding Shrinkage

ISO 294-4

Across Flow

0.80

%

Flow

0.30

%

Water Absorption (Saturation, 23°C)

1.0

%

ISO 62

Water Absorption (E, 23°C, 50% RH)

0.40

%

ISO 62Mechanical

Nominal Value

Unit

Test Method

Tensile Modulus

132

MPa

ISO 527-1

Tensile Stress (Break)

27.0

MPa

ISO 527-2

Tensile Stress

ISO 527-2

--

27.0

MPa

50% Strain

12.0

MPa

Nominal Tensile Strain at Break

450

%

ISO 527-2Impact

Nominal Value

Unit

Test Method

Charpy Notched Impact Strength

ISO 179/1eA

-30°C

No Break

23°C

No Break

Charpy Unnotched Impact Strength

ISO 179/1eU

-30°C

No Break

23°C

No Break

Hardness

Nominal Value

Unit

Test Method

Shore Hardness (Shore D, 3 sec)

46

ISO 7619-1Thermal

Nominal Value

Unit

Test Method

Deflection Temperature Under Load (0.45 MPa, Unannealed)

65.0

°C

ISO 75-2/B

Deflection Temperature Under Load (1.8 MPa, Unannealed)

45.0

°C

ISO 75-2/A

Glass Transition Temperature

-40.0

°C

ISO 11357-2

Vicat Softening Temperature

--

70.0

°C

ISO 306/B

--

140

°C

ISO 306/A

Peak Melting Temperature

157

°C

ASTM D3418

Melting Temperature

157

°C

ISO 11357-3

CLTE - Flow (23 to 55°C)

2.3E-4

cm/cm/°C

ISO 11359-2

CLTE - Transverse (23 to 55°C)

2.1E-4

cm/cm/°C

ISO 11359-2Electrical

Nominal Value

Unit

Test Method

Volume Resistivity

1.0E+9

ohms·m

IEC 62631-3-1

Electric Strength 2

37

kV/mm

IEC 60243-1

Relative Permittivity

IEC 62631-2-1

100 Hz

8.50

1 MHz

4.70

Dissipation Factor

IEC 62631-2-1

100 Hz

0.12

1 MHz

0.13

Flammability

Nominal Value

Unit

Test Method

Flammability Classification

IEC 60695-11-10, -20

1.6 mm

HB

3.0 mm

HB