产品说明:
description: lupoy pc 1200-10 resin is designed for extrusionand injection molding products. it exhibits an excellent physicalproperty balance of heat resistance, transparency and impactstrength.
maincharacteristics: fda, medium viscosity, no mold release agent andno uv absorbers
applications: toys, food utensils and packaging applications
cas:103598-77-2
information provided by lg chemical
物性信息:
物理性能额定值 (公制)额定值 (英制)测试方法比重1.20 g/cc1.20 g/ccastm d792吸水率0.32 %@temperature 23.0 °c
0.32 %@temperature 73.4 °f
e, 50% rh; astm d570
0.15 %@temperature 23.0 °c, time 86400 sec
0.15 %@temperature 73.4 °f, time 24.0 hour
astm d570线性成型收缩率,flow0.00050 - 0.00070 cm/cm0.00050 - 0.00070 in/inastm d955熔体流动速率10 g/10 min@load 1.20 kg, temperature 300 °c
10 g/10 min@load 2.65 lb, temperature 572 °f
astm d1238
机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度(m 级)7373astm d785洛氏硬度(r 级)118118astm d785极限抗拉强度71.0 mpa10300 psiastm d638抗张强度(屈服)60.0 mpa8700 psi50mm/min; astm d638伸长率 (断裂)150 %150 %astm d638屈服伸长率6.0 %6.0 %astm d638拉伸模量2.41 gpa350 ksiastm d638弯曲强度96.0 mpa13900 psiastm d790弯曲模量2.41 gpa350 ksiastm d790悬壁梁缺口冲击强度9.074 j/cm@thickness 3.20 mm, temperature 23.0 °c
17.00 ft-lb/in@thickness 0.126 in, temperature 73.4 °f
0.25 mm notch; astm d256悬壁梁无缺口冲击强度nb@temperature 23.0 °c
nb@temperature 73.4 °f
astm d256落锤总能量87.0 j@thickness 3.20 mm
64.2 ft-lb@thickness 0.126 in
203m/min; astm d3763磨损45@load 1.00 kg
45@load 2.20 lb
[%], cs-10 f wheel, 500 cycles; astm d1044
电气性能额定值 (公制)额定值 (英制)测试方法体积电阻率2.00e+17 ohm-cm2.00e+17 ohm-cmastm d257介电常数3.0@frequency 60.0 hz
3.0@frequency 60.0 hz
astm d150介电强度17.0 kv/mm432 kv/inastm d149耗散因数0.0010@frequency 60.0 hz
0.0010@frequency 60.0 hz
astm d150相比耐漏电起痕指数(cti)250 v@thickness 2.00 mm
250 v@thickness 0.0787 in
iec 112
热性能额定值 (公制)额定值 (英制)测试方法线性热膨胀系数68.0 µm/m-°c@temperature -40.0 - 82.0 °c
37.8 µin/in-°f@temperature -40.0 - 180 °f
astm d696hot ball pressure test>= 125 °c>= 257 °fiec 598-1载荷下热变形温度(0.46 mpa)144 °c@thickness 4.00 mm
291 °f@thickness 0.157 in
annealed; astm d648deflection temperature at 1.8 mpa (264 psi)128 °c@thickness 4.00 mm
262 °f@thickness 0.157 in
unannealed; astm d648
141 °c@thickness 4.00 mm
286 °f@thickness 0.157 in
annealed; astm d648维卡软化温度149 °c@load 5.10 kg
300 °f@load 11.2 lb
50°c/hr; astm d1525软化温度150 - 200 °c302 - 392 °fmelting point per msds可燃性(ul94)hb@thickness 3.00 mm
hb@thickness 0.118 in
astm d635
v-2@thickness 0.500 mm
v-2@thickness 0.0197 in
astm d635
v-2@thickness 1.60 mm
v-2@thickness 0.0630 in
astm d635
v-2@thickness 2.50 - 2.70 mm
v-2@thickness 0.0984 - 0.106 in
astm d635flash point>= 450 °c>= 842 °f
极限氧指数26 %26 %astm d2863灼热丝试验850 °c@thickness 2.00 mm, time 5.00 sec
1560 °f@thickness 0.0787 in, time 0.00139 hour
iec 695-2-1
光学性能额定值 (公制)额定值 (英制)测试方法折射率1.5861.586astm d542雾度0.70 - 1.5 %0.70 - 1.5 %astm d1003transmission, visible89 %89 %astm d1003
材料描述
测试方法autoignition temperature>460°c
average extent of burningastm d635