产品说明:
general purpose grade. good clarity, heat resistance, propertyretention and dimensional stability.
物性信息:
基本信息
黄卡编号e12
特性尺寸稳定性良好
耐热性,高
通用
中等透明度
用途通用
加工方法注射成型
多点数据coefficient of thermal expansion vs. temperature (astm e831)
flexural dma (astm d4065)
pressure-volume-temperature (pvt - zoller method)
shear dma (astm d4065)
specific heat vs. temperature (astm d3417)
tensile creep (astm d2990)
tensile fatigue
tensile stress vs. strain (astm d638)
thermal conductivity vs. temperature (astm e1530)
viscosity vs. shear rate (astm d3835)
物理性能额定值单位制测试方法比重1.20g/cm³astm d792熔流率(熔体流动速率) (300°c/1.2 kg)25g/10 minastm d1238收缩率 - 流动 (3.20 mm)0.50 到 0.70%内部方法吸水率
astm d570 24 hr0.10%astm d570 平衡, 23°c0.35%astm d570 平衡, 100°c0.58%astm d570
机械性能额定值单位制测试方法抗张强度 1
astm d638 屈服62.1mpaastm d638 断裂65.5mpaastm d638伸长率 2(断裂)120%astm d638弯曲模量 3(50.0mm 跨距)2310mpaastm d790弯曲强度 4(屈服,50.0 mm 跨距)93.1mpaastm d790
冲击性能额定值单位制测试方法悬壁梁缺口冲击强度 (23°c)640j/mastm d256装有测量仪表的落镖冲击 (23°c, energy at peakload)54.2jastm d3763拉伸冲击强度 5378kj/m²astm d1822
热性能额定值单位制测试方法载荷下热变形温度 (1.8 mpa, 未退火, 3.20mm)127°castm d648rti elec130°cul 746rti imp130°cul 746rti130°cul 746
电气性能额定值
测试方法相比耐漏电起痕指数(cti)plc 2
ul 746高电弧燃烧指数(hai)plc 1
ul 746高电压电弧起痕速率 (hvtr)plc 2
ul 746热丝引燃 (hwi)plc 2
ul 746
可燃性额定值
测试方法ul 阻燃等级 (1.09 mm)v-2
ul 94
光学性能额定值单位制测试方法透射率 (2540 µm)88.0%astm d1003雾度 (2540 µm)1.0%astm d1003
注射额定值单位制
干燥温度121°c
干燥时间3.0 到 4.0hr
干燥时间,大48hr
建议的大水分含量0.020%
建议注射量40 到 60%
料筒后部温度249 到 271°c
料筒中部温度260 到 282°c
料筒前部温度271 到 293°c
射嘴温度266 到 288°c
加工(熔体)温度271 到 293°c
模具温度71.1 到 93.3°c
背压0.345 到 0.689mpa
螺杆转速40 到 70rpm
排气孔深度0.025 到 0.076mm