hostaform®lx90gc15

acetal (pom) copolymer

celanese corporation

15% 玻璃纤维增强材料

产品说明：

preliminary data sheet
hostaform® lx90gc15 is a specialty metallic appearance acetalcopolymer grade that is integrally colored and has a nominal 15%fiber glass loading. this grade provides additional strength andstiffness over unfilled acetal grades while presenting a metalappearance surface.
besides material, optimal finish for specialty metallic parts isdependent on proper drying, gate design, knit line locations, andspecial processing. please contact celanese technical service forassistance with your application.
chemical abbreviation according to iso 1043-1: pom

物性信息：

基本信息

填料/增强材料	玻璃纤维增强材料, 15% 填料按重量
特性	刚性，良好 良好的强度
rohs 合规性	联系制造商
外观	金属化 - 染色
树脂id (iso 1043)	pom

物理性能额定值单位制测试方法

密度	1.50	g/cm³	iso 1183
收缩率			iso 294-4
垂直流动方向	1.2	%	iso 294-4
流动方向	0.70	%	iso 294-4
吸水率 (饱和, 23°c)	0.85	%	iso 62

机械性能额定值单位制测试方法

拉伸模量	5500	mpa	iso 527-2/1a/1
拉伸应力 (断裂)	75.0	mpa	iso 527-2/1a/5
拉伸应变 (断裂)	4.0	%	iso 527-2/1a/5
弯曲模量 (23°c)	5200	mpa	iso 178

冲击性能额定值单位制测试方法

简支梁缺口冲击强度			iso 179/1ea
-30°c	4.0	kj/m²	iso 179/1ea
23°c	4.0	kj/m²	iso 179/1ea

热性能额定值单位制测试方法

热变形温度
0.45 mpa,未退火	161	°c	iso 75-2/b
1.8 mpa,未退火	155	°c	iso 75-2/a
熔融温度 1	166	°c	iso 11357-3
线形热膨胀系数			iso 11359-2
流动	5.0e-5	cm/cm/°c	iso 11359-2
横向	1.0e-4	cm/cm/°c