马氏体型不锈钢 中国1cr17mn6ni5n 1cr18mn8ni5n 1cr17ni7 1cr18ni9y1cr18ni9 y1cr18ni9se 0cr19ni9 0cr18ni9 00cr19ni10 00cr18ni100cr19ni19n 0cr19ni10nbn 00cr18ni10n 1cr18ni12 1cr18ni12ti 0cr23ni130cr25ni20 1cr25ni20si2 0cr17ni12mo2 0cr17ni13mo2n 0cr18ni12mo2cu200cr18ni14mo2cu2 0cr19ni13mo3 1cr18ni12mo3ti 0cr18ni12mo3ti00cr19ni13mo3 00cr17ni14mo3 0cr18ni16mo5 1cr18ni9ti 0cr18ni11ti0cr18ni9ti 0cr18ni11nb 0cr18ni9cu3 0cr18ni13si4
日本sus201 sus202 sus301 sus302 sus303 sus303se sus304 sus304lsus304n1 sus304n2 sus304ln sus305 sus309s sus310s sus316 sus316lsus316n sus316ln sus316j1 sus316j1l sus317 sus317l sus317j1 sus321sus347 susxm7 sussm15j1
奥氏体-铁素体型不锈钢 中国0cr26ni5mo2 1cr18ni11si4alti 00cr18ni15mo3si2日本329j1 sus329j1
铁素体型不锈钢 中国0cr13al 00cr12 1cr17 ycr17 1cr17mo 00cr30mo200cr27mo 日本sus405 sus410l sus430 sus430f sus434 sus447j1susxm27
马氏体型不锈钢 中国1cr12 0cr13 1cr13 1cr13mo y1cr13 2cr13 3cr13 4cr13y3cr13 1cr17ni2 7cr17 8cr17 11cr17 9cr18 711cr17
沉淀硬化型不锈钢0cr17ni4cu4nb 0cr17ni7al 0cr15ni7mo2al
材料的名称：sus440c不锈钢
标准：jis
(1)模具钢的特性：不锈钢，含铬量高达16%-18%，初被应用于外科手术刀具及船舶业，耐蚀性能力极优，韧性强。含碳量约1%(440系a、b、c及f级；c级及f及含碳量高，而a则较少)，经热处理后硬度可达58hrc。
含碳量1.2%这种钢材的抗锈能力不错，是目前用在批量刀具市场上的不锈钢，其强度及锋利性甚于ats-34，含铬量高达16%-18%，是第二常用的不锈钢(仅次于ats-34)，也是早被刀匠接受的不锈钢，而且一直很受欢迎，尤其是在零下处理流程被开发出来后，这种处理加强了钢材的坚韧度。在打磨时，它的缺点是黏性比较大，而且升温很快，但他比任何碳钢都更容易打磨，用手锯切料也容易得多。440℃的退火温度很低，硬度通常达到56-58hrc，耐蚀性和韧性都很强。
供货状态硬度：退火态，硬度270hbs
化学成分(质量分数%)c：0.95-1.10、mn≤1.00、p≤0.025、si≤1.00、cr：16.0-18.0、mo：0.40-0.70、s≤0.030
应用举例：广泛应用于手制刀及厂制刀具。 泛应用于手制刀及厂制刀具。
SUS440C棒材价格*SUS440C不锈钢板*SUS440C不锈钢热处理硬度