聚苯硫醚PPS 美国泰科纳 6345L4玻纤增强30%+10%PTFE
- 供应商
- 东莞市华韵塑胶原料有限公司
- 认证
- 报价
- ¥48.50元每千克
- PPS
- 聚苯硫醚
- 6345L4
- 玻纤增强30%+10%PTFE
- 美国泰科纳
- 低磨耗 良好的耐磨性
- 联系电话
- 0769-87600377
- 手机号
- 13556776933
- 经理
- 赵琳
- 所在地
- 东莞市樟木头镇奥园塑金国际8栋214
- 更新时间
- 2024-05-29 08:30
聚苯硫醚pps 美国泰科纳 6345l4玻纤增强30%+10%ptfe 低磨耗 良好的耐磨性
等级 | 品名 | 种类 | 说明 |
fortron 0203 | pps | unfilled | low viscosity, for compounding |
fortron 0203hs | pps | unfilled | low viscosity, heat stabilized, for compounding & melt blown extrusion applications |
fortron 0205 | pps | unfilled | medium-range viscosity, for compounding |
fortron 0205b4/20µm | pps | specialty | specialty |
fortron 0214 | pps | unfilled | high viscosity, for extrusion |
fortron 0300 | pps | unfilled | extrusion grade |
fortron 0309 | pps | unfilled | unfilled |
fortron 0317 | pps | unfilled | available as 0317b1 flake, 0317p1 pellets, and 0317c1 crystallized pellet variant. |
fortron 0320 | pps | unfilled | high melt viscosity, for extrusion |
fortron 1115l0 | pps | specialty | fiberglass reinforced with high melt strength for blow molding & extrusion applications |
fortron 1120l4 | pps | specialty | fortron 1120l4 is a 20% glass fiber reinforced injection molding grade. |
fortron 1130l0 | pps | glass reinforced | fortron 1130l0 is a 30% glass-reinforced extrusion grade. |
fortron 1130l4 | pps | glass reinforced | 30% glass reinforced, excellent flow, good weldability, v-0 |
fortron1131l4 itt | pps | glass reinforced | 30% glass reinforced pps, low flash, good weldability, v-0 |
fortron 1140e7 | pps | glass reinforced | 40% glass reinforced, low flash and fast cycling, v-0 |
fortron 1140l0 | pps | glass reinforced | 40% glass reinforced extrusion grade, strong and tough, v-0 |
fortron 1140l4 | pps | glass reinforced | 40% glass reinforced, strong and tough, v-0 |
fortron 1140l6 | pps | glass reinforced | 40% glass reinforced, easy flow, strong and tough, v-0 |
fortron 1140l7 | pps | glass reinforced | 40% glass reinforced, fast cycling, easy flow, v-0 |
fortron 1140lc6 | pps | specialty | low chlorine, 40% gf |
fortron 1141l4 | pps | glass reinforced | 40% glass reinforced pps, low flash, v-0 |
fortron 1200l1 | pps | specialty | unfilled extrusion grade that has a high melt viscosity and tensile elongation. |
fortron 1342l4 | pps | specialty | 40% glass reinforced with ptfe, low wear |
附:物性表(以pps 1140l6 泰科纳为例)
性能项目 试验条件[状态] 测试方法 测试数据 数据单位
基本性能 吸水率 iso 62 0.02 %
物理性能 比重 iso 1183 1.65 g/cm3
模具收缩率 iso 2577 0.2-0.6 %
机械性能 拉伸模量 iso 527-1 14700 mpa
拉伸强度 iso 527-1 195 mpa
断裂伸长率 iso 527-1 1.9 %
弯曲模量 iso 178 14500 mpa
弯曲强度 iso 178 285 mpa
izod缺口冲击强度 23℃ iso 180/1a 10 kj/m2
洛氏硬度 iso 2039-2 100 m-scale
热性能 热变形温度 1.80mpa iso 75-1 270 ℃
阻燃等级 ul94 v-0
pps 1140l6 美国泰科纳的加工注塑:
1)注塑:
可采用通用注塑机,玻璃纤维增强pps的熔融指数以50为宜。注塑的工艺条件为:料筒温度,纯pps为280~330℃,40%gfpps为300-350℃;喷嘴温度,纯pps为305℃,40%gfpps为330℃;模具温度120-180℃;注塑压力,50-130mpa。
2)挤出:
采用排气式挤出机,工艺为:加料段温度小于200℃;料筒温度300-340℃,连接体温度320-340℃,口模温度300-320℃。
3)模压成型:
适合大型制品,采用两次压缩,先冷却,后热压。热压的预热温度纯pps为360℃左右15min,gfpps为380℃左右20min;模压压力为10~30mpa,冷却到150℃脱模。
4)喷涂成型:
采用悬浮喷涂法和悬浮喷涂与干粉热喷混合法,都是将pps喷涂到金属表面,再经过塑化、淬火处理而得到涂层;pps的涂层处理温度在300℃以上,保温30min。