evatane®24-03

ethylene vinyl acetate copolymer

arkema

产品说明：

evatane® 24-03 is a random copolymer of ethylene and vinylacetate made by high-pressure radicalar polymerization process.
the high vinyl acetate content of evatane® 24-03 brings softness,flexibility and polarity. evatane® 24-03 delivers high cohesivestrength with most fillers and can be used to produce masterbatchesor hffr compounds, and can be used as an additive for bitumenmodification. evatane® 24-03 is also suitable for film (cast orblown) extrusion, and exhibits good adhesion onto pe, ps andpolyesters.

物性信息：

基本信息

特性	良好的柔韧性 良好粘结性 柔软 无规共聚物
用途	blown film 沥青改性 流延薄膜 母料
形式	粒子
加工方法	吹塑薄膜 挤出 浇铸

物理性能额定值单位制测试方法

密度 (23°c)	0.940	g/cm³	iso 1183
熔流率（熔体流动速率） (190°c/2.16 kg)	2.5 到 3.5	g/10 min	astm d1238, iso 1133
醋酸乙烯含量	23.0 到 25.0	wt%

硬度额定值单位制测试方法

肖氏硬度 (邵氏 a)	83		astm d2240, iso 868

机械性能额定值单位制测试方法

抗张强度 (断裂)	27.0	mpa	astm d638, iso 527-2
伸长率 (断裂)	600 到 900	%	astm d638, iso 527-2

热性能额定值单位制测试方法

维卡软化温度	46.0	°c	iso 306/a, astm d1525 1
熔融温度	80.0	°c	iso 11357-3
ring and ball softening point 2	183	°c	astm e28

eva中，va含量5%-40%左右，eva有很好的弹性和柔韧度，耐低温抗冲击性能好，可以在寒冷低温零下40-60度使用；热封性能好，熔点低；我公司又va含量3%，va含量5%，va含量8%，va含量10%，va含量12%，va含量15%，va含量18%，va含量20%，va含量25%，va含量30%，va含量40%的eva材料。    
        eva用于薄膜，可以提高薄膜的抗穿刺性能，做pp和pe塑料的增韧剂，发泡鞋材，鞋底，管子，汽车油管，型材，包装膜，热熔胶，玩具，色母载体，低烟无卤电线电缆，改性用，儿童玩具，瑜伽垫，塑料地板，汽车配件，发泡产品，拼豆豆，凉鞋，洞洞鞋，油墨，涂料，胶水。