耐撕裂 tpu 德国巴斯夫 1185a10 抗菌性 耐磨 食品接触 挤出级聚醚

elastollan®1185a10

thermoplastic polyurethane elastomer (polyether)

basf corp. thermoplastic polyurethanes

产品说明：

elastollan® 1185a is specifically formulated for extrudedprofile, sheet and film applications. it exhibits excellentabrasion resistance, toughness, transparency, very good lowtemperature flexibility, hydrolytic stability and fungusresistance. it has excellent damping characteristics andoutstanding resistance to tear propagation. elastollan® 1185a10 israted ul-94 hb in vertical flame test for wall thickness of 1.5 mm.elastollan® 1185a also conforms to the fda food contact section,book 21, section 177.2600. elastollan® 1185a also has nsf standard61 "water contact material" certification. elastollan® 1185a issupplied uncolored in diced or pelletized form.

物性信息：

基本信息

特性	低温下的柔性 抗菌性 良好的撕裂强度 良好耐磨损性 韧性良好 食品接触的合规性 水解稳定
机构评级	fda 21 cfr 177.2600 nsf 61
外观	清晰/透明
加工方法	挤出 注射成型

物理性能额定值单位制测试方法

比重	1.12	g/cm³	astm d792
熔流率（熔体流动速率）			astm d1238
190°c/21.6kg	1.0 到 20	g/10 min	astm d1238
190°c/8.7kg	1.0 到 10	g/10 min	astm d1238

硬度额定值单位制测试方法

肖氏硬度 (邵氏 a)	85		astm d2240

机械性能额定值单位制测试方法

拉伸模量 (注塑)	20.7	mpa	astm d412
弯曲模量 (注塑)	29.0	mpa	astm d790
泰伯耐磨性	30.0	mg	astm d1044
abrasion - din	25	mm³	din 53516

热性能额定值单位制测试方法

softening point - dma	66	°c	内部方法

弹性体额定值单位制测试方法

拉伸应力			astm d412
应变	9.65	mpa	astm d412
300%应变	21.4	mpa	astm d412
抗张强度	35.9	mpa	astm d412
伸长率 (断裂)	530	%	astm d412
撕裂强度 1	110	kn/m	astm d624
压缩yongjiu变形			astm d395b
23°c, 22hr	25	%	astm d395b
70°c, 22hr	45	%	astm d395b

热性能额定值单位制测试方法

玻璃转化温度	-38.0	°c	内部方法
维卡软化温度	100	°c	astm d1525

可燃性额定值
测试方法

ul 阻燃等级 (1.50 mm)	hb		ul 94