polyamide 12
lati s.p.a.
碳纳米填料
产品说明：
partially conductive/dissipative compound based onpolyamide 12 (pa 12).
carbon nanotubes.
| 密度 | 1.02 | g/cm³ | iso 1183 |
| 收缩率 1 | iso 294-4 | ||
| 垂直流动方向 : 2.00 mm | 1.8 到 2.2 | % | iso 294-4 |
| 流动方向 : 2.00 mm | 1.6 到 2.0 | % | iso 294-4 |
| 拉伸模量 (23°c) | 1900 | mpa | iso 527-2/1 |
| 拉伸应力 (断裂, 23°c) | 50.0 | mpa | iso 527-2/5 |
| 拉伸应变 (断裂, 23°c) | 7.0 | % | iso 527-2/5 |
| 简支梁缺口冲击强度 (23°c) | 8.0 | kj/m² | iso 179/1ea |
| 简支梁无缺口冲击强度 (23°c) | 60 | kj/m² | iso 179/1eu |
| 悬壁梁缺口冲击强度 (23°c) | 80 | j/m | astm d256a |
| 热变形温度 | |||
| 0.45 mpa, 未退火 | 120 | °c | iso 75-2/b |
| 1.8 mpa, 未退火 | 55.0 | °c | iso 75-2/a |
| 维卡软化温度 | 150 | °c | iso 306/b50 |
| 表面电阻率 | 10 | ohms | astm d257 |
| 干燥温度 | 70.0 到 90.0 | °c | |
| 干燥时间 | 3.0 | hr | |
| 加工（熔体）温度 | 190 到 220 | °c | |
| 模具温度 | 70.0 到 90.0 | °c | |
| 注射速度 | 中等 |
| 1 . | at 60 mpa of cavity pressure |
产品 供货地区 产品说明
latiohm 57d-05 pd01 g/15 partiallyconductive/dissipative compound based on...
latiohm 62-03 pd01 g/20 partially conductive/dissipativecompound based on...
latiohm 62-08 pd02 g/30 dissipative compound based onpolyamide 6 (pa 6). ...
latiohm 62-09 pd01 g/20-v2hf dissipative compound basedon polyamide 6 (pa 6). ...
latiohm 63-08 pd02 g/25 dissipative compound based onpolyamide 6 (pa 6), ...
latiohm 66-04 pd01 g/25-v0ct1 partiallyconductive/dissipative compound based on...
latiohm 66-05 pd01 g/20 partially conductive/dissipativecompound based on...
latiohm 66-06 pd03 g/20 partially conductive/dissipativecompound based on...
latiohm 66-07 pd08 g/30 semiconductive/dissipativeproduct based on polyam...
latiohm 66-08 pd02 g/35 dissipative compound based onpolyamide 66 (pa 66)...
latiohm 66-10 h2 cnt ce/10 dissipative compound based onpolyamide 66 (pa 66)...
latiohm 66-10 h2 cnt g/35 partiallyconductive/dissipative compound based on...
latiohm 82-01 cnt partially conductive/dissipativecompound based on...
展开全文