PA66德国巴斯夫8202HS热稳定耐磨损薄壁产品应用

          pa66德国巴斯夫8202hs热稳定耐磨损薄壁产品应用

  

   

物性表

物理性能测试条件测试方法测试结果单位收缩率md：3.18mm
1.2%吸水率24hrastmd5701.6%23°c,24hriso621.6%饱和astmd5709.5%饱和,23°ciso629.5%平衡,50%rhastmd5702.7%平衡,23°c,50%rhiso622.7%机械性能测试条件测试方法测试结果单位拉伸模量23°ciso527-22700mpa80°ciso527-2485mpa120°ciso527-2360mpa150°ciso527-2290mpa抗张强度屈服,-40°castmd638126mpa屈服,23°castmd63879.0mpa屈服,80°castmd63835.0mpayield,121°castmd63825.0mpa拉伸应力屈服,-40°ciso527-2126mpa屈服,23°ciso527-278.0mpa屈服,80°ciso527-235.0mpa弯曲模量23°castmd7902830mpa65°castmd790500mpa90°castmd790350mpa121°castmd790305mpa23°ciso1782400mpa弯曲强度-40°castmd790170mpa23°castmd790108mpa65°castmd79030.0mpa90°castmd79020.0mpa121°castmd79017.0mpa拉伸应力屈服,120°ciso527-225.0mpa屈服,150°ciso527-220.0mpa抗张强度断裂,23°castmd63875.0mpa伸长率屈服,23°castmd6384.0%屈服,80°castmd63842%yield,121°castmd63836%拉伸应变屈服,23°ciso527-24.0%伸长率断裂,23°castmd63855%标称拉伸断裂应变23°ciso527-225%弯曲模量-40°castmd7903010mpa弯曲应力23°ciso17885.0mpa热性能测试条件测试方法测试结果单位rtiimp1.5mmul746105°c3.0mmul746105°c6.0mmul746105°crtistr0.71mmul74695.0°c1.5mmul746105°c3.0mmul746105°c6.0mmul746105°c热变形温度0.45mpa,未退火astmd648178°c0.45mpa,未退火iso75-2/b150°c1.8mpa,未退火astmd64865.0°c1.8mpa,未退火iso75-2/a60.0°c熔融峰值温度
astmd3418220°c溶融温度（dsc）
iso3146220°c线形热膨胀系数mdastme8318.3e-05cm/cm/°crtielec0.71mmul746130°c1.5mmul746130°c3.0mmul746130°c6.0mmul746130°crtiimp0.71mmul74695.0°c电气性能测试条件测试方法测试结果单位介电强度
iec60243-137kv/mm漏电起痕指数
iec60112600vvolumeresistivity1.50mmastmd257>1.0e+13ohms·cm体积电阻率
iec60093>1.0e+13ohms·cm介电强度21.50mmastmd14922kv/mm冲击性能测试条件测试方法测试结果单位简支梁无缺口冲击强度-30°ciso17951kj/m²23°ciso179nobreak
落下冲击阻力23°c内部方法142j
-40°castmd25648j/m23°castmd25658j/m23°ciso1793.5kj/m²硬度测试条件测试方法测试结果单位洛氏硬度r级astmd785119
可燃性测试条件测试方法测试结果单位ul阻燃等级0.71mmul94v-2
1.5mmul94v-2
3.0mmul94v-2
6.0mmul94v-2