抗uv 耐候 8267ghs 德国巴斯夫 pa6 低翘曲 高刚性 矿物增强 车轮汽车外部零件

ultramid®8267g hs bk-106

polyamide 6

basf corporation

40% 玻璃矿物

产品说明：

ultramid 8267g hs bk-106 is a heat stabilized, weatherresistant, 40% mineral and glass fiber reinforced pa6 injectionmolding compound with improved uv resistance and sink markresistance. the combination of mineral and glass fibers result in ahigh performance, low warp and cost effective engineeringthermoplastic. it exhibits high strength, good uv resistance,rigidity and good heat distortion temperatures. it has a relativelyhigh resistance to creep under load. the heat stabilizer systemextends its retention of properties at elevated temperatures. ithas good chemical resistance to greases, oils and hydrocarbons.
applications
ultramid 8267g hs bk-106 is generally recommended for applicationssuch as rotors, wheels, rims, timing belt covers, automotivecooling fans, shrouds and all external parts exposed to theenvironment.

物性信息：

基本信息

填料/增强材料	玻璃\矿物, 40% 填料按重量
添加剂	热稳定剂
特性	低翘曲性 刚性，高 高强度 抗紫外线性能良好 良好的抗蠕变性 耐化学性良好 耐气候影响性能良好 耐碳氢化合物 耐油性能 耐油脂性能 热稳定性
用途	车轮 汽车领域的应用 汽车外部零件
机构评级	ec 1907/2006 (reach)
rohs 合规性	rohs 合规
外观	黑色
形式	粒子
加工方法	注射成型

物理性能额定值单位制测试方法

比重	1.48	g/cm³	astm d792, iso 1183
收缩率 - 流动 (3.18 mm)	0.40	%
吸水率
24 hr	0.90	%	astm d570
23°c, 24hr	0.90	%	iso 62
饱和	5.7	%	astm d570
饱和, 23°c	5.7	%	iso 62
平衡, 50%rh	1.6	%	astm d570
平衡, 23°c, 50%rh	1.6	%	iso 62

硬度额定值单位制测试方法

洛氏硬度 (r 级)	121		astm d785

机械性能额定值单位制测试方法

拉伸模量			iso 527-2
-40°c	10800	mpa	iso 527-2
23°c	9200	mpa	iso 527-2
80°c	3090	mpa	iso 527-2
121°c	2620	mpa	iso 527-2
抗张强度
断裂, -40°c	178	mpa	astm d638, iso 527-2
断裂, 23°c	125	mpa	astm d638
断裂, 80°c	59.0	mpa	astm d638, iso 527-2
断裂, 121°c	51.0	mpa	astm d638, iso 527-2
断裂, 23°c	115	mpa	iso 527-2
伸长率
断裂, -40°c	3.0	%	astm d638
断裂, 23°c	2.0	%	astm d638, iso 527-2
断裂, 80°c	13	%	astm d638
断裂, 121°c	11	%	astm d638
弯曲模量
23°c	7580	mpa	astm d790
23°c	7200	mpa	iso 178
弯曲强度
23°c	200	mpa	astm d790
23°c	178	mpa	iso 178