polyphthalamide (ppa), 30% glass fiber reinforced
dupont performance polymers
产品说明:
30% glass reinforced flame retardant non-halogenated ppa highperformance polyamide
zytelhtnfr52g30nh bk337 is a 30% glass reinforced flame retardantlubricated high performance polyamide resin. it is also a ppa resinand it uses a non-halogenated fla
information provided by dupont performance polymers
物性信息:
密度 | 1.44 g/cc | 0.0520 lb/in³ | dam; iso 1183 |
线性成型收缩率,flow | 0.0030 cm/cm | 0.0030 in/in | dam; iso 294-4 2577 |
线性成型收缩率,横向 | 0.010 cm/cm | 0.010 in/in | dam; iso 294-4 2577 |
抗张强度(断裂) | 150 mpa | 21800 psi | dam; iso 527-1/-2 |
抗张强度 | 0.150 mpa @strain 0.000 %, temperature 175 °c | 21.8 psi @strain 0.000 %, temperature 347 °f | dam; iso 11403-1 -2 |
0.180 mpa @strain 0.000 %, temperature 150 °c | 26.1 psi @strain 0.000 %, temperature 302 °f | dam; iso 11403-1 -2 | |
10.49 mpa @strain 0.200 %, temperature 150 °c | 1521 psi @strain 0.200 %, temperature 302 °f | 50%rh; iso 11403-1 -2 | |
12.22 mpa @strain 0.110 %, temperature 40.0 °c | 1772 psi @strain 0.110 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
13.56 mpa @strain 0.110 %, temperature 23.0 °c | 1967 psi @strain 0.110 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
13.67 mpa @strain 0.110 %, temperature -40.0 °c | 1983 psi @strain 0.110 %, temperature -40.0 °f | 50%rh; iso 11403-1 -2 | |
15.62 mpa @strain 0.130 %, temperature 23.0 °c | 2265 psi @strain 0.130 %, temperature 73.4 °f | dam; iso 11403-1 -2 | |
18.0 mpa @strain 0.150 %, temperature -40.0 °c | 2610 psi @strain 0.150 %, temperature -40.0 °f | dam; iso 11403-1 -2 | |
30.39 mpa @strain 0.760 %, temperature 175 °c | 4408 psi @strain 0.760 %, temperature 347 °f | dam; iso 11403-1 -2 | |
33.24 mpa @strain 0.680 %, temperature 150 °c | 4821 psi @strain 0.680 %, temperature 302 °f | dam; iso 11403-1 -2 | |
33.35 mpa @strain 0.830 %, temperature 150 °c | 4837 psi @strain 0.830 %, temperature 302 °f | 50%rh; iso 11403-1 -2 | |
44.64 mpa @strain 0.450 %, temperature 40.0 °c | 6474 psi @strain 0.450 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
45.48 mpa @strain 1.46 %, temperature 175 °c | 6596 psi @strain 1.46 %, temperature 347 °f | dam; iso 11403-1 -2 | |
47.11 mpa @strain 1.49 %, temperature 150 °c | 6833 psi @strain 1.49 %, temperature 302 °f | 50%rh; iso 11403-1 -2 | |
47.7 mpa @strain 0.420 %, temperature 23.0 °c | 6920 psi @strain 0.420 %, temperature 73.4 °f | dam; iso 11403-1 -2 | |
48.18 mpa @strain 0.440 %, temperature 23.0 °c | 6988 psi @strain 0.440 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
49.15 mpa @strain 1.26 %, temperature 150 °c | 7129 psi @strain 1.26 %, temperature 302 °f | dam; iso 11403-1 -2 | |
55.18 mpa @strain 2.30 %, temperature 175 °c | 8003 psi @strain 2.30 %, temperature 347 °f | dam; iso 11403-1 -2 | |
55.38 mpa @strain 2.19 %, temperature 150 °c | 8032 psi @strain 2.19 %, temperature 302 °f | 50%rh; iso 11403-1 -2 | |
56.61 mpa @strain 0.490 %, temperature -40.0 °c | 8211 psi @strain 0.490 %, temperature -40.0 °f | 50%rh; iso 11403-1 -2 | |
61.01 mpa @strain 1.99 %, temperature 150 °c | 8849 psi @strain 1.99 %, temperature 302 °f | dam; iso 11403-1 -2 | |
61.84 mpa @strain 0.550 %, temperature -40.0 °c | 8969 psi @strain 0.550 %, temperature -40.0 °f | dam; iso 11403-1 -2 | |
64.29 mpa @strain 4.64 %, temperature 150 °c | 9324 psi @strain 4.64 %, temperature 302 °f | 50%rh; iso 11403-1 -2 | |
66.07 mpa @strain 5.37 %, temperature 175 °c | 9583 psi @strain 5.37 %, temperature 347 °f | dam; iso 11403-1 -2 | |
67.98 mpa @strain 0.760 %, temperature 40.0 °c | 9860 psi @strain 0.760 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
71.24 mpa @strain 0.660 %, temperature 23.0 °c | 10330 psi @strain 0.660 %, temperature 73.4 °f | dam; iso 11403-1 -2 | |
74.37 mpa @strain 4.87 %, temperature 150 °c | 10790 psi @strain 4.87 %, temperature 302 °f | dam; iso 11403-1 -2 | |
74.82 mpa @strain 0.740 %, temperature 23.0 °c | 10850 psi @strain 0.740 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
85.4 mpa @strain 1.06 %, temperature 40.0 °c | 12400 psi @strain 1.06 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
90.43 mpa @strain 0.830 %, temperature -40.0 °c | 13120 psi @strain 0.830 %, temperature -40.0 °f | 50%rh; iso 11403-1 -2 | |
91.62 mpa @strain 0.860 %, temperature -40.0 °c | 13290 psi @strain 0.860 %, temperature -40.0 °f | dam; iso 11403-1 -2 | |
93.25 mpa @strain 1.00 %, temperature 23.0 °c | 13520 psi @strain 1.00 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
95.43 mpa @strain 0.950 %, temperature 23.0 °c | 13840 psi @strain 0.950 %, temperature 73.4 °f | dam; iso 11403-1 -2 | |
116.94 mpa @strain 1.15 %, temperature -40.0 °c | 16961 psi @strain 1.15 %, temperature -40.0 °f | 50%rh; iso 11403-1 -2 | |
118.43 mpa @strain 2.11 %, temperature 40.0 °c | 17177 psi @strain 2.11 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
119.69 mpa @strain 1.18 %, temperature -40.0 °c | 17360 psi @strain 1.18 %, temperature -40.0 °f | dam; iso 11403-1 -2 | |
135.95 mpa @strain 1.94 %, temperature 23.0 °c | 19718 psi @strain 1.94 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
156.87 mpa @strain 2.06 %, temperature 23.0 °c | 22752 psi @strain 2.06 %, temperature 73.4 °f | dam; iso 11403-1 -2 | |
178.43 mpa @strain 2.12 %, temperature -40.0 °c | 25879 psi @strain 2.12 %, temperature -40.0 °f | 50%rh; iso 11403-1 -2 | |
196.69 mpa @strain 2.46 %, temperature -40.0 °c | 28528 psi @strain 2.46 %, temperature -40.0 °f | dam; iso 11403-1 -2 | |
伸长率 (断裂) | 2.2 % | 2.2 % | dam; iso 527-1/-2 |
拉伸模量 | 10.0 gpa | 1450 ksi | dam; iso 527-1/-2 |
弯曲强度 | 230 mpa | 33400 psi | dam; iso 178 |
弯曲模量 | 8.70 gpa | 1260 ksi | dam; iso 178 |
割线模量 | 2.27 gpa @strain 3.27 %, temperature 100 °c | 329 ksi @strain 3.27 %, temperature 212 °f | 50%rh; iso 11403-1 -2 |
3.04 gpa @strain 2.27 %, temperature 100 °c | 441 ksi @strain 2.27 %, temperature 212 °f | 50%rh; iso 11403-1 -2 | |
3.38 gpa @strain 2.84 %, temperature 100 °c | 491 ksi @strain 2.84 %, temperature 212 °f | dam; iso 11403-1 -2 | |
3.90 gpa @strain 1.47 %, temperature 100 °c | 565 ksi @strain 1.47 %, temperature 212 °f | 50%rh; iso 11403-1 -2 | |
4.38 gpa @strain 1.95 %, temperature 100 °c | 636 ksi @strain 1.95 %, temperature 212 °f | dam; iso 11403-1 -2 | |
5.2029 gpa @strain 0.690 %, temperature 100 °c | 754.63 ksi @strain 0.690 %, temperature 212 °f | 50%rh; iso 11403-1 -2 | |
5.36 gpa @strain 1.24 %, temperature 100 °c | 777 ksi @strain 1.24 %, temperature 212 °f | dam; iso 11403-1 -2 | |
5.55 gpa @strain 2.07 %, temperature 80.0 °c | 804 ksi @strain 2.07 %, temperature 176 °f | dam; iso 11403-1 -2 | |
6.46 gpa @strain 1.73 %, temperature 40.0 °c | 937 ksi @strain 1.73 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
6.56 gpa @strain 0.660 %, temperature 100 °c | 951 ksi @strain 0.660 %, temperature 212 °f | dam; iso 11403-1 -2 | |
6.68 gpa @strain 0.120 %, temperature 100 °c | 969 ksi @strain 0.120 %, temperature 212 °f | 50%rh; iso 11403-1 -2 | |
6.70 gpa @strain 1.46 %, temperature 80.0 °c | 971 ksi @strain 1.46 %, temperature 176 °f | dam; iso 11403-1 -2 | |
7.4937 gpa @strain 1.27 %, temperature 40.0 °c | 1086.9 ksi @strain 1.27 %, temperature 104 °f | 50%rh; iso 11403-1 -2 | |
7.88 gpa @strain 1.57 %, temperature 23.0 °c | 1140 ksi @strain 1.57 %, temperature 73.4 °f | 50%rh; iso 11403-1 -2 | |
7.90 gpa @strain 0.950 %, temperature 80.0 °c | 1150 ksi @strain 0.950 %, temperature 176 °f | dam; iso 11403-1 -2 | |
8.07 gpa @strain 0.180 %, temperature 100 °c | 1170 k |