PC 1303AH-10含UV稳定剂易脱模用于户外用品汽车灯

韩国lg化学一级代理商，价格电议。

 特性： 含uv稳定剂，中粘，脱模良好，listed on ameca
 应用： 户外应用，汽车大灯
                                                                                  1303ah-10
       测试项目                                                测试方法    单位       数值
        melt flowrate(300℃/1.2kg)                          astm d1238 g/10min      10
       density                                              astmd792              1.2
        moldshrinkage                                       astm d955   mm/mm   0.005-0.007
        water absorption@24hrs,23℃                          astm d570    %        0.15
                       @e,50%rh,23℃              astm d570    %        0.32
        refractiveindex,no                                  astmd542             1.586
        lighttransmittance                                  astm d1003   %         89
       haze                                                 astm d1003    %      0.7-1.5
        deflection temperatureunderload(dtul)@4mm          astm d648     ℃
         @66psi(0.45mpa),annealed                           astm d648    ℃        144
         @264psi(1.8mpa),annealed                           astm d648    ℃        141
         @264psi(1.8mpa),unannealed                         astm d648    ℃        128
        vicat softeningpoint,50℃/hr,50nload               astm d1525   ℃        149
        coefficient of linearthermal expansion,@-40 to 82℃  astm d696  mm/mm/℃ 68×10-6

        tensile yieldstrength                               astm d638   mpa        60
        ultimate tensilestrength                            astm d638   mpa        71
        elongation atyield                                  astm d638    %          6
        elongation atbreak                                  astm d638    %         150
        tensilemodulus                                      astm d638    mpa      2410
        flexuralstrength                                    astm d790   mpa        96
        flexuralmodulus                                     astm d790    mpa      2410
        notched izod impact@23℃                            astm d256   j/m        900
        unnotched izod impact@23℃                          astmd256           no break
        instrumented dartimpact,total energy@23℃          astm d3763   j         87
        rockwellhardness                                    astm d785  m scale      73
        taber abrasionresistance(△haze)                   astm d1044   %         45

        ul-94@0.5mm                                         astmd635               -
        ul-94@1.6mm                                         astmd635              hb
        ul-94@2.5-2.7mm                                     astmd635               -
        ul-94@3.0mm                                         astmd635              hb
        limiting oxygenindex                                astm d2863   %         26
        ball indentationtemperature                         iec598-1     ℃       >125
        average extent ofburning                            astm d635    mm        25

       gwt2.0mm,5second                                     iec695-2-1   ℃        850
        comparative trackingindex@2.0mm                     iec112       v         250
        dielectricstrength                                  astm d149   kv/mm      17
        eielectric constant@60hz                            astmd150               3
        dissipation factor@60hz                              astmd150             0.001
        volume resistivity@23℃,dry                         astm d257   Ω-cm    2.0×1017