产品说明：

acrymid® tt70 is a highly heat distortion-resistantpoly(n-methyl methacrylimide) (pmmi).
besides showing the properties common to all acrymid® moldingcompounds, such as

excellent transmission and clarity,

very high mechanical strength and rigidity,

good weather resistance.

acrymid® tt70 has the following specific characteristics:

high stability of the optical characteristics at long-lastingthermal load,

highest heat deflection temperature under load.

application:
acrymid® molding compound is particularly suitable for injectionmolding of items meant for applications that involve maximumthermal loads.

物理性能额定值单位制测试方法

密度	1.21	g/cm³	iso 1183
溶化体积流率（mvr） (260°c/10.0 kg)	1.70	cm³/10min	iso 1133
吸水率 (平衡, 23°c, 50% rh)	6.0	%	iso 62

机械性能额定值单位制测试方法

拉伸模量	4000	mpa	iso 527-2/1
拉伸应力 (断裂)	80.0	mpa	iso 527-2/5
拉伸应变 (断裂)	3.0	%	iso 527-2/5

冲击性能额定值单位制测试方法

简支梁无缺口冲击强度 (23°c)	20	kj/m²	iso 179/1eu

热性能额定值单位制测试方法

热变形温度
0.45 mpa, 未退火	158	°c	iso 75-2/b
1.8 mpa, 未退火	149	°c	iso 75-2/a
维卡软化温度	170	°c	iso 306/b50

可燃性额定值
测试方法

ul 阻燃等级 (1.60 mm)	hb		ul 94
fire rating	b2		din 4102

光学性能额定值单位制测试方法

折射率	1.540		iso 489
透射率	91.0	%	iso 13468-2

注射额定值单位制

干燥温度	< 150	°c
干燥时间	2.0 到 3.0	hr
加工（熔体）温度	260 到 290	°c
模具温度	130	°c

高耐热 pmma 德国赢创德固赛 tt70 高光级 

供应

pmma德国赢创德固赛8n 

pmma德国赢创德固赛8ndf23 

pmma德国赢创德固赛df23-8n 

pmma德国赢创德固赛8803

pmma德国赢创德固赛8ndf22 

pmma德国赢创德固赛zk6hf 

pmma德国赢创德固赛7n 

pmma德国赢创德固赛8805

pmma德国赢创德固赛8809

pmma德国赢创德固赛8813

pmma德国赢创德固赛8817

pmma德国赢创德固赛8967

pmma德国赢创德固赛zk4br 

pmma德国赢创德固赛zk6br 

pmma德国赢创德固赛6n 

pmma德国赢创德固赛8ndf21 

pmma德国赢创德固赛tt70 

pmma德国赢创德固赛ft15 

pmma德国赢创德固赛hw55 

pmma德国赢创德固赛7h 

pmma德国赢创德固赛df 8n20 

pmma德国赢创德固赛df22-8n 

pmma德国赢创德固赛zk5hf 

pmma德国赢创德固赛375

pmma德国赢创德固赛8h 

pmma德国赢创德固赛zk30 

pmma德国赢创德固赛zk40 

pmma德国赢创德固赛8n 0v200 

pmma德国赢创德固赛8n 0v606 

pmma德国赢创德固赛8n-33691 

pmma德国赢创德固赛8n-8v106 

pmma德国赢创德固赛8n-90114 

pmma德国赢创德固赛df21-8n 

pmma德国赢创德固赛8n rot 33691 

pmma德国赢创德固赛g20-100 

pmma德国赢创德固赛zk5br