PC 6267防火（PC阻燃）德国科思创

拜耳物 pc6267 性表

physical propertiesmetricenglishcomments
density 1.20 g/cc0.0434 lb/in³iso 1183
1.02 g/cc
@temperature 280 °c0.0368 lb/in³
@temperature 536 °fmelt
water absorption 0.30 %0.30 %similar to iso62
moisture absorption at e 0.12 %0.12 %similar to iso62
linear mold shrinkage, flow 0.0070 cm/cm0.0070 in/inparallel; iso294-4,2577
linear mold shrinkage, transverse 0.0070 cm/cm0.0070 in/iniso294-4,2577
melt flow 19 g/10min
@load 1.20 kg,
temperature 300 °c19 g/10min
@load 2.65 lb,
temperature 572 °fiso 1133
mechanical propertiesmetricenglishcomments
tensile strength, yield 67.0 mpa9720 psiiso 527-1/-2
elongation at break >= 50 %>= 50 %nominal; iso527-1/-2
elongation at yield 6.0 %6.0 %iso 527-1/-2
tensile modulus 2.45 gpa355 ksiiso 527-1/-2
charpy impact unnotched nbnbiso 179/1eu
 nb
@temperature -30.0 °cnb
@temperature -22.0 °fiso 179/1eu
impact 50005000puncture -maximum force (n); iso 6603-2
 5900
@temperature -30.0 °c5900
@temperature -22.0 °fpuncture -maximum force (n); iso 6603-2
puncture energy 50.0 j36.9 ft-lbiso 6603-2
55.0 j
@temperature -30.0 °c40.6 ft-lb
@temperature -22.0 °fiso 6603-2
electrical propertiesmetricenglishcomments
volume resistivity >= 1.00e+13 ohm-cm>= 1.00e+13 ohm-cmiec 60093
surface resistance >= 1.00e+15 ohm>= 1.00e+15 ohmiec 60093
dielectric constant   3.0
@frequency 1.00e+6 hz3.0
@frequency 1.00e+6 hziec 60250
3.1
@frequency 100 hz3.1
@frequency 100 hziec 60250
dielectric strength 34.0 kv/mm864 kv/iniec 60243-1
dissipation factor   0.00080
@frequency 100 hz0.00080
@frequency 100 hziec 60250
0.0090
@frequency 1.00e+6 hz0.0090
@frequency 1.00e+6 hziec 60250
comparative tracking index 225 v225 viec 60112
thermal propertiesmetricenglishcomments
cte, linear, parallel to flow 65.0 µm/m-°c36.1 µin/in-°fiso11359-1/-2
cte, linear, transverse to flow 65.0 µm/m-°c36.1 µin/in-°fiso11359-1/-2
specific heat capacity 1.70 j/g-°c0.406 btu/lb-°fmelt
thermal conductivity 0.173 w/m-k1.20 btu-in/hr-ft²-°fmelt
deflection temperature at 0.46 mpa (66 psi) 134 °c273 °fiso 75-1/-2
deflection temperature at 1.8 mpa (264 psi) 122 °c252 °fiso 75-1/-2
vicat softening point 144 °c291 °f50°c/h 50n; iso306
flammability, ul94   v-0
@thickness 1.50 mmv-0
@thickness 0.0591 iniec60695-11-10
v-0
@thickness 3.00 mmv-0
@thickness 0.118 iniec60695-11-10
oxygen index 35 %35 %iso4589-1/-2
processing propertiesmetricenglishcomments
melt temperature 280 °c536 °finjectionmolding; iso 294
280 - 320 °c536 - 608 °f
mold temperature 80.0 °c176 °finjectionmolding; iso 10724
80.0 - 120 °c176 - 248 °f
ejection temperature 130 °c266 °f
injection velocity 200 mm/sec7.87 in/seciso 294
descriptive propertiesavailabilityasia pacific
europe
india
neareast/africa
northamerica
south and centralamerica
eff. thermal diffusivity (m²/s)1e-07
featurelight stabilisedor stable to light
releaseagent
u.v. stabilisedor stable to weather
formpellets
processinjectionmolding
ul recognitionul\l1.5\n
ul\lh\n