聚偏氟乙烯(pvdf)是一种半晶态铁电聚合物, 目前，已测得pvdf的晶型有5种。相、β相、γ相、ε

相及ρ相。各种晶体结构的生成取决于加工条件，在一定条件(如拉伸、极化、浇注等处理方法)下，这些晶相

之间可以互相转变。α相是5种晶型中能量低，稳定的结构，pvdf由液态缓慢冷却或由溶液流延形成薄

膜时，通常都形成α相。经过拉伸、电极化后形成的日相pvdf显示出强的压电、热释电性质。pvdf具有较

宽的工作温度范围，其体电阻高、质量轻、柔顺性好，且机械强度高、频响宽。

arkemagroup kynar® 9000 hd polyvinylidene fluoride - injectionmolding

polyvinylidinefluoride (pvdf), molded/extruded

arkema

产品说明：

characteristics: natural resin -translucent, off-white hemispheres. high stability in harshthermal, chemical and ultraviolet environments. high toughness andmechanical strength, low permeability, abrasion resistance; highpurity

applications:

chemical processing – production, storage and transfer ofcorrosive fluids

electronics – protective sheathing, plenum and wiringinsulation

semi-conductor industry

food stuff and healthcare industries

transportation – fuel line and pipe, thermoformed bodycomponents

information provided by arkema inc.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

体积密度	0.961 g/cc	0.0347 lb/in³
粘度	500000 - 800000 cp @shear rate 100 1/s, temperature 232 °c	500000 - 800000 cp @shear rate 100 1/s, temperature 450 °f	melt viscosity; astm d3835
熔体流动速率	16 - 40 g/10 min @load 5.00 kg, temperature 232 °c	16 - 40 g/10 min @load 11.0 lb, temperature 450 °f	astm d1238

热性能额定值 (公制)额定值 (英制)测试方法

熔融温度	165 - 172 °c	329 - 342 °f

加工性能额定值 (公制)额定值 (英制)测试方法

料筒后部温度	190 - 210 °c	374 - 410 °f	injection molding
料筒中部温度	200 - 220 °c	392 - 428 °f	injection molding
料筒前部温度	200 - 240 °c	392 - 464 °f	injection molding
射嘴温度	200 - 240 °c	392 - 464 °f	injection molding
模具温度	50.0 - 90.0 °c	122 - 194 °f	injection molding