泰科纳 PA66 长玻璃纤维PA66-GF50-02 P7 低翘曲性锦纶66塑料胶粒
- 供应商
- 东莞市越泰新材料有限公司
- 认证
- 报价
- ¥28.00元每千克
- 泰科纳
- 15 g/10 min
- GF50-0
- 熔指10
- 美国
- 9.0 kJ/m²
- 联系电话
- 180-98275951
- 手机号
- 13450060513
- 经理
- 龙军
- 所在地
- 东莞市樟木头莞樟路23号五号
- 更新时间
- 2024-05-01 08:10
泰科纳 pa66 长玻璃纤维pa66-gf50-02 p7 低翘曲性锦纶66塑料胶粒
polyamide 66
celanese corporation
50% 长玻璃纤维
产品说明:
material code according to iso 1043-1: pa66
heat stabilized nylon 66 reinforced by 50 weight percent longglass
fibers. the pellets are cylindrical and normally as well as the
embedded fibers 7 mm long.
parts molded of celstran have outstanding mechanical propertiessuch
as high strength and stiffness combined with high heatdeflection.
the notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. thelong
fiber reinforcement reduces creep significantly.
the very isotropic shrinkage in the molded parts minimizes the
warpage.
complex parts can be manufactured with high reproducibility by
injection molding.
can be used for substituting die cast metal with the advantageof
weight reduction, no corrosion problems, no post treatment.
物性信息:
填料/增强材料 | 长玻璃纤维, 50% 填料按重量 |
添加剂 | 热稳定剂 |
特性 | 低翘曲性 刚性,高 高强度 抗撞击性,良好 良好的抗蠕变性 耐低温冲击 热稳定性 |
用途 | 金属取代 |
rohs 合规性 | 联系制造商 |
形式 | 粒子 |
加工方法 | 注射成型 |
树脂id (iso 1043) | pa66 |
密度 | 1.57 | g/cm³ | iso 1183 |
拉伸模量 | 16600 | mpa | iso 527-2/1a/1 |
拉伸应力 (断裂) | 260 | mpa | iso 527-2/1a/5 |
拉伸应变 (断裂) | 2.1 | % | iso 527-2/1a/5 |
熔融温度 1 | 260 | °c | iso 11357-3 |
干燥温度 | 70.0 到 80.0 | °c | |
干燥时间 | 2.0 到 4.0 | hr | |
建议的*大水分含量 | 0.15 | % | |
料斗温度 | 70.0 到 80.0 | °c | |
料筒后部温度 | 280 到 285 | °c | |
料筒中部温度 | 280 到 290 | °c | |
料筒前部温度 | 290 到 300 | °c | |
射嘴温度 | 310 到 320 | °c | |
加工(熔体)温度 | 310 到 320 | °c | |
模具温度 | 90.0 到 120 | °c | |
注塑压力 | 120 到 150 | mpa | |
注射速度 | 中等 | ||
保压 | 50.0 到 80.0 | mpa | |
背压 | 0.00 到 3.00 | mpa |