ESTANE路博润TPU 58315

estane tpu 58315具有非常好的物理性能、抗水解性、低温性能和耐磨性。宽的挤出加工窗口。

用途：吹塑和平模/流延膜挤出、注塑和电缆护套。

very good physical properties, hydrolysis resistance, lowtemperature performance and abrasion. wide processing window forextrusion.

uses: blown and flat die/cast film extrusion, injection moldingand cable jacketing.

tpu 58315的加工参数：

物理性能额定值 (公制)额定值 (英制)测试方法

比重	1.12 g/cc	1.12 g/cc	astm d792
处理	0.020	0.020

机械性能额定值 (公制)额定值 (英制)测试方法

肖氏硬度 (邵氏 a)	82 - 88@time 5.00 sec	82 - 88@time 0.00139 hour	astm d2240
抗张强度	48.3 mpa	7010 psi	astm d412
	33.81 mpa@temperature 75.0 °c, time 4.838e+6 sec	4904 psi@temperature 167 °f, time 1344 hour	30 mil sheet, immersion in water
	39.12 mpa@temperature 75.0 °c, time 605000 sec	5674 psi@temperature 167 °f, time 168 hour	30 mil sheet, immersion in water
	39.12 mpa@temperature 75.0 °c, time 1.21e+6 sec	5674 psi@temperature 167 °f, time 336 hour	30 mil sheet, immersion in water
	46.85 mpa@temperature 75.0 °c, time 2.82e+6 sec	6795 psi@temperature 167 °f, time 784 hour	30 mil sheet, immersion in water
	48.3 mpa@temperature 75.0 °c, time 0.000 sec	7010 psi@temperature 167 °f, time 0.000 hour	30 mil sheet, immersion in water
伸长率 (断裂)	570 %	570 %	astm d412
300％模量	0.0103 gpa	1.49 ksi	astm d412
撕裂强度	26.3 kn/m	150 pli	trosuer; astm d470
graves tear strength	85.9 kn/m	490 pli	die c; astm d624
泰伯磨损，毫克/1000次	37	37	h18, 1000g; astm d3389 b
tensile set	14 %	14 %	200% elongation; astm d412

热性能额定值 (公制)额定值 (英制)测试方法

熔融温度	135 °c	275 °f	dsc
	145 °c	293 °f	kofler
玻璃化转变温度，tg	-50.0 °c	-58.0 °f	dsc

光学性能额定值 (公制)额定值 (英制)测试方法

雾度	1.8 %	1.8 %	pressed between glass; astm d1003

加工性能额定值 (公制)额定值 (英制)测试方法

1区	171 °c	340 °f	extrusion
2区	177 °c	351 °f	extrusion
3区	182 °c	360 °f	extrusion
4区	188 °c	370 °f	extrusion
adapter temperature	188 °c	370 °f	5, extrusion
模具温度	188 °c	370 °f	6, zone 1, extrusion
	188 °c	370 °f	zone 2, extrusion
干燥温度	104 °c	219 °f
干燥时间	2.00 - 4.00 hour	2.00 - 4.00 hour
霜点	-40.0 °c	-40.0 °f